South africa chrome ore lumpy is a highly fireproof sharpener for moulds and cores. Originally from South Africa. The sand is produced by crushing chrome ore and its washing in spiral concentrators, subsequent drying, dust cleaning, screening and sorting as per grain size. Chemical composition Cr2O3 46.0%min SiO2 1.0%max FeO 26.5%max CaO 0.3%max MgO 10.0%max Al2O3 15.5%max P 0.003%max S 0.003%max Cr/Fe 1.55/1 Physical composition Bulk Density 2.5-3g/cm3 Specific Gravity 4.0-4.8g/cm3 PH Value 7-9 The amount of the acid 2ML max Percent soil 0.1%max The sintered 1600 Filling Density 2.6g/cm3 melting temperature 2180°C
South africa chrome ore lumpy is a highly fireproof sharpener for moulds and cores. Originally from South Africa. The sand is produced by crushing chrome ore and its washing in spiral concentrators, subsequent drying, dust cleaning, screening and sorting as per grain size. Chemical composition Cr2O3 46.0%min SiO2 1.0%max FeO 26.5%max CaO 0.3%max MgO 10.0%max Al2O3 15.5%max P 0.003%max S 0.003%max Cr/Fe 1.55/1 Physical composition Bulk Density 2.5-3g/cm3 Specific Gravity 4.0-4.8g/cm3 PH Value 7-9 The amount of the acid 2ML max Percent soil 0.1%max The sintered 1600 Filling Density 2.6g/cm3 melting temperature 2180°C
Lumpy Cr203 39.48% base, Cr/Fe ratio 2.21/1min, Sio2 6% max, Al203 13-16%, MGO 13-16% Feo 15.18% Comcentrate Cr203 47.75% base, Cr/Fe ratio 2.29/1min, Sio2 12-14% max, Al203 13-16%, MGO 17-20% Feo 19.48%
South Africa Chrome Ore sand AFS shipment from China Port Cr2O3:46.0%min SiO2:1.0%max FeO:26.5%max CaO:0.30%max MgO:10.0%max Al2O3:15.5%max P:0.003%max S:0.003%max PACKING:1MT big bag SIZES:AFS 25-35 AFS25-30 AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65
40% above chromite ore. Bulk or plastic
Cr around 42% Fe 15%max Al2o3 3% max Sio2 4% max P 0.05% max S 0.05% max Cr/fe: 2.5:1 min Size 10-300mm Quantity 3000mt Port of discharge: tianjin xingang Shipment: in bulk or in containers
Chorme ore. In bulk
Ferro chorium Guaranteed specs Cr: 60%min C:6-8% si:2.5%max s:0.025%max p:0.03%max Size:10-50mm or 10-100 90%min Delivery date: Within 30 days shipment after receiving TT paymentPacking: In 1mt PVC woven bag in 20' containers
Ferro chrome Cr60%min, c0.06%max, si1.50%max, p0.04%max, s 0.03%max 1mt wowen bag
Chromite Sand - AFS 50 Cr2O3 Fe2O3 MgO Al2O3 SiO2 CaO Na2O K2O 46-48% 24-27% 9-11% 15-18% 0.5-1.0% Max 0.05% Max 0.01% Max 0.01% Chromite Sand - AFS 45 Cr2O3 Fe2O3 MgO Al2O3 SiO2 CaO Na2O K2O 45% 29% 9-11% 16% 1.0% Max 0.2% Max 0.01% Max 0.01% Contact person: Danny Tao
What is ferrochrome? Ferrochromium is made using metallurgical grade chrome ore and can be divided into three categories, depending on the level of carbon in the alloy. The three types of ferrochrome alloys are: High-carbon (HC) ferrochrome (carbon content between 4% and 9%) Low- and medium-carbon (LC & MC) ferrochrome (carbon content less than 0.5% for LC and between 0.5% and 4% for MC) Ferrochrome-silico-chrome (FeSiCr) Ferrochrome applications: Production of steel, especially stainless steel with chromium content of 10 to 20%, is the largest consumer of high-carbon ferrochrome. Over 80% of the worldâ??s ferrochrome is used in the production of stainless steel. The vast majority of ferrochrome produced is� charge chrome, which has a lower chrome content ratio. Used most commonly in stainless steel. Low carbon� and� medium carbon� ferrochrome is used in the manufacture of special steels. Low carbon ferrochrome can be used to produce superalloys.
Ceramic Foundry Sand with the high quality bauxite as the raw material, blowing into the ball after remelting smelting, is a new type of steel casting foundry sand.Itâ??s characteristic as high temperature resistant,small amount of thermal expansion, easy collapse, good renewable performance,good casting properties, received the recognition from the cast made experts domestic and overseas. Widely used in all kinds of casting method,sand casting, special casting( casting, solid type, evaporative pattern casting, ladle flow guiding sand and so on ).Also used for shot peening, low expansion of high-temperature coated sand producing. 200mesh-270mesh used for evanescent mode coating producing. Adding 10-35% can effectively increase the air permeability, and suitable for using all kinds of casting binder.It has been used by numerous domestic and international cast iron and nonferrous metal casting production factories. Ceramic Foundry Sand Technical Specification: 1.Chemical composition: AL2O3â?¥75% Fe2O3â?¤3% K2Oâ?¤1% TiO2â?¤4% , the others: very low 2.Grain Shape: Ball 3.Colour: Brownish black 4.Density: 1.95-2.05 ( g/cm3) 5.Refractory temperature:1850â?? 6.Thermal expansion Rate:0.13% 7.Size: 10-20meshã??20-30meshã??30-40meshã??40-70meshã??100-140meshã??170mesh with the high quality bauxite as the raw material, blowing into the ball after remelting smelting, is a new type of steel casting foundry sand.Itâ??s characteristic as high temperature resistant,small amount of thermal expansion, easy collapse, good renewable performance,good casting properties, received the recognition from the cast made experts domestic and overseas. Widely used in all kinds of casting method,sand casting, special casting( casting, solid type, evaporative pattern casting, ladle flow guiding sand and so on ).Also used for shot peening, low expansion of high-temperature coated sand producing. 200mesh-270mesh used for evanescent mode coating producing. Adding 10-35% can effectively increase the air permeability, and suitable for using all kinds of casting binder.It has been used by numerous domestic and international cast iron and nonferrous metal casting production factories. Ceramic Foundry Sand Technical Specification: 1.Chemical composition: AL2O3 75% Fe2O3 3% K2O 1% TiO2 4% , the others: very low 2.Grain Shape: Ball 3.Colour: Brownish black 4.Density: 1.95-2.05 ( g/cm3) 5.Refractory temperature:1850 6.Thermal expansion Rate:0.13% 7.Size: 10-20mesh 20-30mesh 30-40mesh 40-70mesh100-140mesh 170mesh
Ceramic Foundry Sand with the high quality bauxite as the raw material, blowing into the ball after remelting smelting, is a new type of steel casting foundry sand.It is characteristic as high temperature resistant,small amount of thermal expansion, easy collapse, good renewable performance,good casting properties, received the recognition from the cast made experts domestic and overseas. Widely used in all kinds of casting method,sand casting, special casting( casting, solid type, evaporative pattern casting, ladle flow guiding sand and so on ).Also used for shot peening, low expansion of high-temperature coated sand producing. 200mesh-270mesh used for evanescent mode coating producing. Adding 10-35% can effectively increase the air permeability, and suitable for using all kinds of casting binder.It has been used by numerous domestic and international cast iron and nonferrous metal casting production factories. Ceramic Foundry Sand Technical Specification: 1.Chemical composition: AL2O3 75% Fe2O3 3% K2O 1% TiO2 4% , the others: very
Ceramic Foundry Sand with the high quality bauxite as the raw material, blowing into the ball after remelting smelting, is a new type of steel casting foundry sand.It is characteristic as high temperature resistant,small amount of thermal expansion, easy collapse, good renewable performance,good casting properties, received the recognition from the cast made experts domestic and overseas. Widely used in all kinds of casting method,sand casting, special casting( casting, solid type, evaporative pattern casting, ladle flow guiding sand and so on ).Also used for shot peening, low expansion of high-temperature coated sand producing. 200mesh-270mesh used for evanescent mode coating producing. Adding 10-35% can effectively increase the air permeability, and suitable for using all kinds of casting binder.It has been used by numerous domestic and international cast iron and nonferrous metal casting production factories. Ceramic Foundry Sand Technical Specification: 1.Chemical composition: AL2O3 75% Fe2O3 3% K2O 1% TiO2 4% , the others: very
Ceramic Foundry Sand with the high quality bauxite as the raw material, blowing into the ball after remelting smelting, is a new type of steel casting foundry sand.It is characteristic as high temperature resistant,small amount of thermal expansion, easy collapse, good renewable performance,good casting properties, received the recognition from the cast made experts domestic and overseas. Widely used in all kinds of casting method,sand casting, special casting( casting, solid type, evaporative pattern casting, ladle flow guiding sand and so on ).Also used for shot peening, low expansion of high-temperature coated sand producing. 200mesh-270mesh used for evanescent mode coating producing. Adding 10-35% can effectively increase the air permeability, and suitable for using all kinds of casting binder.It has been used by numerous domestic and international cast iron and nonferrous metal casting production factories. Ceramic Foundry Sand Technical Specification: 1.Chemical composition: AL2O3 75% Fe2O3 3%
Ceramic Foundry Sand Ceramic Foundry Sand with the high quality bauxite as the raw material, blowing into the ball after remelting smelting, is a new type of steel casting foundry sand.It is characteristic as high temperature resistant,small amount of thermal expansion, easy collapse, good renewable performance,good casting properties, received the recognition from the cast made experts domestic and overseas. Widely used in all kinds of casting method,sand casting, special casting( casting, solid type, evaporative pattern casting, ladle flow guiding sand and so on ).Also used for shot peening, low expansion of high-temperature coated sand producing. 200mesh-270mesh used for evanescent mode coating producing. Adding 10-35% can effectively increase the air permeability, and suitable for using all kinds of casting binder.It has been used by numerous domestic and international cast iron and nonferrous metal casting production factories. Ceramic Foundry Sand Technical Specification: 1.Chemical composition: AL2O3 75% Fe2O3 3% K2O 1% TiO2 4% , the others: very
Cr 60%min, C0.06%max, Si1.5%max,P0.04%max,S0.03%max
Chromite Sand is a naturally occurring spinel consisting primarily of the oxides of chrome and iron. It is a by-product of ferro-chrome production and is mainly used in foundry applications and in glass production. Cr2O3:46.0% min SiO2:1.0%max FeO:26.5%max CaO:0.30% max MgO:10.0% max Al2O3:15.5%max P:0.003% max S:0.003% max SIZES: AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65 PACKING: 1MT big bag
Chromite sand wholesale price 46% Chromite Sand AFS40-45 Chromite Sand is a naturally occurring spinel consisting primarily of the oxides of chrome and iron. It is a by-product of ferro-chrome production and is mainly used in foundry applications and in glass production. Cr2O3:46.0%min SiO2:1.0%max FeO:26.5%max CaO:.30%max MgO:10.0%max Al2O3:15.5%max P:0.003%max S:0.003%max SIZES:AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65 PACKING:1MT big bag
Ladle filler sand/chromite price/chromite chrome ore 46% Cr2O3 Chromite Sand is a naturally occurring spinel consisting primarily of the oxides of chrome and iron. It is a by-product of ferro-chrome production and is mainly used in foundry applications and in glass production. Cr2O3:46.0%min SiO2:1.0%max FeO:26.5%max CaO:.30%max MgO:10.0%max Al2O3:15.5%max P:0.003%max S:0.003%max SIZES:AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65 PACKING:1MT big bag