Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 °C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Material: HDPE (High Density Polyethylene) Grade: Blown Film Melt Flow Index: 0.3 to 0.5 g/10min Density: 0.951 g/cm3 Packing: Jumbo Bags on Pallets Loading Port: Jeddah, Saudi Arabia Loading Capacity: 25 to 28 TONS Origin: Saudi Petrochemical Industry
MATERIAL : HDPE Film A Grade CATEGORY :HDPE TYPE :Film GRADE :A SPECIFICATION :HDPE has a slight stain on the surface due to the press machine.Has some lables ORIGIN : Japan LOADING WEIGHT : 18-20 Tons CNF (USD/Ton) : " $580 -780 Haiphong $530 - 730 Malaysia "
Item Test Condition Test Method Value Unit MFR 190C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Material: Hdpe Plastic Granules Color: Natural Tea Color Application: Plastic bag packing film grade Density: 0.940~0.976 G/cm3
JPE HDPE Off grade MFR: Package:25kg Quantity:100MT Loading Weight: 26T