Chequered Plywood

Magnus compreg plywood is a premium grade ply which confirms to the standards of IS:3513 & manufactured under extremely high pressure in high tonnage hydraulic presses. Application: The plywood has strong screw holding capability, used for making boxes for the heavy equipments, electrical transformers, fish storage boxes, marine decks & cabins etc. Compreg plywood can be used for manufacturing of pallets for industrial application and railway berths & seats etc. Thicknesses : 4 to 100 mm Size : 600 to 3200 mm in length 600 to 1675 mm in width Density : 0.95 to 1.4 gm/cm3 TECHNICAL SPECIFICATIONS (IS:3513:1989) Test BIS Requirements Magnus Results Specific gravity test (i) Medium density 0.95 To 1.25 1.25 (ii) High density 1.25 To 1.35 1.35 Adhesive IS 848 �­2006 BWP Moisture contents 6 To 12% 7.5% Tensile strength (High density) GH (V) 155 MPa 180 MPa (VI) 90 MPa 115 MPa (Medium density) GM (V) 108 MPa 125 MPa (VII) 59 MPa 80 MPa Static banding strength (High density) GH (V) 145 MPa 170 MPa (VI) 100 MPa 140 MPa (Medium density) GH (V) 88 MPa 110 MPa (VI) 59 MPa 90 MPa Compressive strength a) Parallel to laminates 165 MPa (High density) GH (V) 130 MPa 125 MPa (VI) 90 85 MPa (Medium density) GM (V) 55 115 MPa (VI) 75 b) Perpendicular to laminate 105 MPa (High density) GH (V) 70 MPa 195 MPa (VI) 160 103 MPa (Medium density) GM (V) 70 170 (VI) 130 Shear strength (High density) GH (V) 14 MPa 20 MPa Parallel to laminate (VI) 14 MPa 19 MPa Perpendicular to laminate (V) 60 MPa 78 Mpa (VI) 45 MPa 61 Mpa Hardness (rockwell 'H' scale) (High density) GH (VI) 80 MPa 95 Mpa (Medium density) GM (VI) 60 MPa 75 Mpa 2 Impact strength (Kgm/cm ) (High density) GH Parallel to laminate (VI) 0.5 0.6 Perpendicular to laminate (VI) 0.3 0.4 (Medium density) GM Parallel to laminate (VI) 0.5 0.62 Perpendicular to laminate (VI) 0.2 0.28

Mould & die plywood is produced by highly technical precision process environment. All the measuring instruments used in this process are calibrated and are latest quality products. Input of raw materials like veneer, resin and chemicals are segregated and tested before processing to ensure their quality. All the timber logs of selected species like dipterocarp us [Gurjan (keruing)], fagus sylvatica (steam beach) etc. are given steam treatment to take out the oil and soften the fiber for precision peeling on peeling lathe. This product is cured under digital controlled parameters to maintain all the chemical & mechanical properties. Application: Moulds for molding techniques like, injection molding, blow molding, transfer molding rotational molding, casting, patterns, profiles, extrude, die etc. Thickness : 25 to 200 mm Sizes : 1220 x 120 to 1675 x 3200 mm 3 Density : 0.95 to 1.40 gm/cm Adhesive : BWP grade, IS 848:2006 TECHNICAL SPECIFICATIONS Properties BIS Requirements Observation IS 3513 : 1989 Values 1. Dimensions a. Length 2440mm 2442mm b. Width 1220mm 1222mm c. Squareness 2% 1mm d. Edge straightness 2% 0.95mm e. Thickness 35mm 35.15mm 3 2. Density 0.95 to 1.25 gm/cm 1.20 gm/cm 3. Moisture contents 6 to 12% 7.50% 4. Physical properties a. Tensile strength 59MPa 140 MPa b. Static bending MOR 59MPa 170 MPa c. Compressive strength parallel to laminate 75MPa 120 MPa d. Perpendicular to laminate 130 MPa 170 MPa e. Hardness test hardness on rockwell H scale 60 65 2 2 f. Impact strength parallel to laminate 0.5kg. M/cm 0.58kg. �­M/cm 2 2 g. Perpendicular to laminate 0.2kg. M/cm 0.29kg.M/cm i Thickness swelling (3% Max) within 4 hours 0.40% Max water soaking with in 4 hours 1.50 % Max

Magnus film faced shut tering plywood is manufactured with high density timber in ultra modern hot presses. Since it is manufactured with CPGL technology, thus it has extra strength than ordinary film face ply. For structurally strong and better bonding it is treated differently while manufacturing. Magnus film face shuttering ply is widely known for the maximum repetitions it gives. Users find it a very useful & economical product worth their investment. TECHNICAL SPECIFICATIONS (IS:4990:1993) Dimension BIS Requirement Observation Values 1 Length 2440 + 6 2442mm 2. Width 1220 + 3 1222mm 3. Thickness 12mm ± 5% 11.90mm 4. Squareness 2mm/1000 mm 0.95mm 5. Edge straightness 2mm/1000mm 0.50mm Physical properties 6. Density 0.95 0.95 7. Moisture contents 5 -­ 15% 7.50% 8. Adhesion of plies (in dry state) Some adherent fibre distributed Satis factory more or less uniformly 9. Adhesion of plies (in wet state) do Satisfactory 10. Glue shear strength (in dry state) vg.­ 1350N 1520N Ind. ­ 1100N 1190N 11. Glue shear strength (in wet state) vg. ­ 1000N 1260N Ind. ­ 800N 900N 2 2 12. Tensile strength Along the grain 480kg./cm 525kg./cm 2 2 Across the grain 340kg./cm 370kg./cm 2 2 Total 820kg./cm 895kg./cm 13. Static bending strength 2 2 along the grain M.O.E.A vg. ­ 7500N/mm 8420N/mm 2 2 ind. ­ 6700N/mm 6975/mm 2 2 Across the grain M.O.E.Avg. 4000N/mm 4800N/mm 2 2 Ind. 3600N/mm 4000N/mm2 Along the grain M.O.R.Avg.50 68N/mm 2 Ind. ­ 45 50N/mm 2 Across the grain M.O.R. Avg. 30 47N/mm 2 Ind. 27 31N/mm 3 3 14. Retention of preservative (ACC) 12 kg/m 12.95 kg/gm 15. My cological test (a) Visual inspection (a) Show no separation sign (b) Glue shear strength Avg. 1000 N 1260 N Adhesion of plies Ind.­ 800 N 910 Adherent fibre distributed Satisfactory Special features of Magnus film faced shuttering plywood are: Magnus film faced shuttering plywood is most effective in RCC constructions. It has a smooth mirror like superior finishing on both surfaces. It saves up to 45% of cost compared to other similar products due to more repetition during shuttering work. Its cross laminated structure between face veneer, core veneer and the film again enhances the strength of ply. After using it as shuttering plywood for many times, it can be re�used for paneling, roofing, flooring, partitions etc.

Magnus futuristic LVL is an engineered wood product, manufactured by compressing multiple layers of thin wood. These are much less likely than conventional lumber to warp, twist, bow, or shrink due to its composite nature. Being highly stable dimensionally, these products are used for headers, beams, and edge ­forming material. Nowa­days, door and window frames where wood was used, is also replaced by LVL. Application : Shuttering, supports,beams, header, edge forming door frame, window frames, construction with wood. Size : 2440, 2745, 3050 and 3200 mm Thicknesses : 25, 37.5, 50, 75, 62.5, 100, 150, 200 mm 3 Density : 0.65 to 1.20 gm/cm

Magnus HBEAMS are designed and fabricated as per international standards. It is manufactured in such a way that it can bear heavy loads. HÃ? BEAMS are engineere wooden product which consists two flanges and one web beam. Flanges are purely light weight with high strength whereas web beams are made up of plywood or sandwich wood. Applications : H Beams are used where require heavy load such as ceilings, walls, bridges, tunnels, platforms, structure, shuttering, platforms, formworks, columns etc Sizes (Length) : 1200, 1800, 2450, 2750, 3050, 3200, 3650, 3950, 4270, 4570, 4600, 4880, 6100 mm Advantages : Chamfered corners, multi repetitions, high load bearing capacity, standard shape as per international norms, corners covered withplastic caps etc.

Magnus chequered plywood is one of the best transportation purpose plywood. The ply has a chequered pattern on its surface. Because of high pressure, the panel develops high density that can sustain high traffic on flooring in public & industrial use Application: This is an antis kid plywood which is useful in flooring specially in heavy vehicles and large containers. It is useful in automobile sector for ceiling, paneling, seat back rest etc. Thicknesses : 12, 15, 19 & 25 mm Weight : 33 & 36 Kg in 12 mm, 38 & 44 Kg in 15 mm Sizes : 5.5 x 2.5 feet to 10.5 x 5.5 feet

Magnus chemical grade plywood is made by thin layered veneers of wood. The species of wood is used to produce this plywood are selected, high densities, oil and decay free, matured and high strength. It has got excellent resistance to moisture, concentrated acids and alkalies, climate vagaries, wear and tear etc. It is a unique and versatile engineering material. Magnus compregs are wood based synthetic resin laminates panel finds extensive application in industries where mechanical strength and resistance to moisture and chemical degradation are required. APPLICATIONS: Magnus Compreg Plywood For Chemical Industry are extensively used by various chemical industries like Fertilizer, Solvent Extraction, Zinc Plants, Vanaspati Plants, Pharmaceuticals Refineries, Synthetic Resin Plants etc. Thickness Available : 4 Mm To 100 Mm (depending Upon Customer's Requirement). Sizes Available : 3 Length (in Mm): 600 To 3200 Width (in Mm): 300 To 1675 �?¢ Density (in Mm): 1.25 To 1.4 Gm/cm

FIRE RETARDANT PLY FOR PRE­FABRICATED HOUSES AND BUILDINGS Magnus plywood for prefabricated houses is the high strength and all weather vagaries resistant plywood. It is made by hardwood species with single core veneer and using BWP grade E1 (Emission Level) standard adhesive for its internal bonding. It is suitable to human health due to free from formaldehyde emission. All the veneers are processed by jet type hot air dryers for its moisture equalization and uniform properties. This plywood is double pressed by cold and heating medium for high mechanical strength. APPLICATIONS: Useful for Prefabricated houses structural materials like roofs, walls, racks, slabs, floorings, partitions, false ceilings, storage spaces etc. THICKNESS AVAILABLE (IN MM): 3,6, 9, 12, 16, 19, & 25 3 Sizes Available: Length In Mm: 1220 To 3200 Width In Mm: 300 To 1675 Density : 0.65 To 0.75 Gm/cm

Our Specially created Fire Retardant Plywood delays temperature rise, reduce the evaporation of gases, prevent the oxygen content and flame spread. Fire Retardant Plywood can be used in places where there are chances of catching fire like kitchens, restaurants. Applications: container, buses, trucks, railway, hotels multistoried buildings, offices, shopping mall, cinema hall, pantry cars, kitchen etc. Fire Retardant Treatment : type 1 & type 2 Size : 5.5x2.5 to 10.5x5.5 feet Thickness : 4,6,9,12,18,25 mm 3 Density : 0.65 to 1.20 gm/cm TECHNICAL SPECIFICATIONS (IS:5509:2000) Dimensions BIS Requirements Observation Values 1. Length 2440 + 6 2442mm 0 2. Width 1220 + 3 1222mm 0 3. Thickness 12mm �± 5% 11.80mm 4. Squareness 2mm/1000mm 0.95mm 5. Edge straightness 2mm/1000mm 0.50mm 6. Workmanship & finish As per clause 9.1 to 9.2 Satisfactory Physical properties 3 7. Density 0.60 - 0.65gm/cm 0.64gm/cm 8. Moisture contents 5 - 20% 10.25% 9. Water resistance test Pass standard Excellent Cyclic test :8 hours - 16 hours Boiling : drying 3 Cycles : 10. Mycological Test Pass standard Excellent 11. Static bending strength 2 Along the grain M.O.E. Avg. 5000N/mm 5850 N/mm 2 2 Ind. 4500N/mm 4020 N/mm 2 2 Across the grain M.O.E. Avg. 2500N/mm 3480 N/mm 2 2 Ind. 2200N/mm 2855 N/mm 2 Along the grain M.O.R. Avg. 40 47.80N/mm2 Ind. 36 36.40N/mm2 Across the grain M.O.R. Avg. 20 27.25N/mm2 Ind. 18 20.35N/mm FIRE RETARDANT TESTS IS : 5509 : 2000 12. Flammability 30 Min. 35 Min. 13. Flame penetration 30 Min. 33 Min. 14 Rate of burning 20 Min. 28 Min. (Wt. loss 30 to 70%)