Screw And Barrel For Extruder Machine

Specification: Screw diameter: d15- d 300 L/d ratio: 15-46 Product classification: Aiming at different plastic products the screw can be chosen from: general type, pin type, barrier type, separation type, and gas-exhausting type, etc. Base materials: (1)38crmoala(jis sacm645) (2)42crmo(aisi 4140) (3)4cr5mosi v1 (jis skd-61) (4)9cr18mov (5)hpt Bimetallic alloy materials: 1)fe-based alloy 2)ni-based alloy/deloro alloy 3)co-based alloy 4)nico-based alloy 5)tungsten carbide/wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: >950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm Slushing oil coated& film wrapped in wooden case

Specification: Screw Diameter: D15- D 300 L/D ratio: 15-46 Product classification: Aiming at different plastic products the screw can be chosen from: General type, pin type, barrier type, separation type, and gas-exhausting type, etc. Base Materials: (1)38CrMoAlA(JIS SACM645) (2)42CrMo(AISI 4140) (3)4Cr5MoSi V1 (JIS SKD-61) (4)9Cr18MOV (5)HPT Bimetallic alloy materials: 1)Fe-based alloy 2)Ni-based alloy/Deloro alloy 3)Co-based alloy 4)NiCo-based alloy 5)Tungsten carbide/Wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000HV Nitrided brittleness: less than grade 1 Surface roughness: Ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: >950HV Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm Slushing Oil Coated& Film Wrapped in Wooden Case

Specification: Screw diameter: d20mm-d220mm Mould clamping force: 250t-3200t Shot weight: 30g-30000g Technical information Base materials: (1)38crmoala(jis sacm645) (2)42crmo(aisi 4140) (3)4cr5mosi v1 (jis skd-61) (4)9cr18mov (5)hpt Bimetallic alloy materials: 1)fe-based alloy 2)ni-based alloy/deloro alloy 3)co-based alloy 4)nico-based alloy 5)tungsten carbide/wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: ¡ã 950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm. Slushing oil coated& film wrapped in wooden case

Specification: Screw diameter: d20mm- d220mm Mould clamping force: 250t-3200t Shot weight: 30g-30000g Base materials: (1)38crmoala(jis sacm645) (2)42crmo(aisi 4140) (3)4cr5mosi v1 (jis skd-61) (4)9cr18mov (5)hpt Bimetallic alloy materials: 1)fe-based alloy 2)ni-based alloy/deloro alloy 3)co-based alloy 4)nico-based alloy 5)tungsten carbide/wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: 950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm. Slushing oil coated& film wrapped in wooden case

Bimetallic screws Rigidity: HRC56~62 Applicable temperature: below 350 Applicable plastic materials: PA, PPT, PA with fiberglas, ABS, PC Applicable plastic products recommended: PA, ABC, PC Predominance: screw ridge surface wearable, perfect in adding less than 30% fiberglass and regenerate additive In wooden case

Parallel twin screw In wooden case

Specification: 45/90, 45/100, 50/105, 51/105, 55/110, 55/120, 58/124, 60/125, 65/120, 65/132, 68/143, 70/135, 70/140, 75/150, 80/143, 80/156, 92/188 The above are standard specifications, we can customize according to customers' requirements. The compression ratio of screws can be designed according to different products and ingredients. Base materials: 1)38crmoala(jis sacm645) 2)42crmo(aisi 4140) 3)4cr5mosi v1 (jis skd-61) 4)9cr18mov 5)hpt Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: ¡ý 950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm Slushing oil coated& film wrapped in wooden case

Screw diameter: 35mm-200mm Length: less than 10000mm Barrel diameter: 35mm-200mm Material: 38crmoala; skd61; skd11; 40cr; 42crmo; high quality alloy steel Technology for tin coated screw barrel/: nitriding treatment, alloy coating spraying, heat-treatment, quenching Appliance for tin coated screw barrel/: pa, evoh, eaa, pc etc

250~3200KN Mould Clamping Force, 30-25000g Shot Weight Diameter of screw: ¬ª20~¬+200 Screw can be mated with different heads, and barrel can be mated with different nozzles. Nitrided Hardness: HV900-1000 Nitrided case depth: 0.45mm-0.7mm Alloy hardness: HRC50-65 Alloy Depth: 0.8mm-2.0mm Materials: Quality 38CrMoAlA Advanced nitriding process Corrosion&Abrasion resistance bimetal spraying process