Aisi 1045 steel, sae 1045 material
Chemical composition of sae 1045 material
Grade c% mn% si% p% s%
S45c 0.42~0.48 0.6~0.9 0.15~0.35 â?¤0.030 â?¤0.030
Equivalent grade:
Chinese american german japanese
Gb aisi din jis
45# 1045 1.1191 s45c
Available sizes
Round: dia. 60â?? 300mm
Plate: thickness 16 â?? 300mm, width 60- 520mm
Delivery condition: hot rolled or forged peeled or black surface, annealed or no heat treatment.
Properties:
A medium carbon steel is used when greater strength and hardness is desired than in the â??as rolledâ? condition. Extreme size accuracy, straightness and concentricity combine to minimize wear in high speed applications. Turned ground and polished.
Applications:
Component parts for vehicles, shafts, bushings, crankshafts, connecting rods and parts for the machine building industry and steel for axes, knives, hammers etc.
aisi 1045 steel,sae 1045 material Chemical composition of sae 1045 material Grade C% Mn% Si% P S S45C 0.42~0.48 0.6~0.9 0.15~0.35 â?¤0.030 â?¤0.030 Equivalent Grade: Chinese American German Japanese GB AISI DIN JIS 45# 1045 1.1191 S45C Available sizes Round: Dia. 60â?? 300mm Plate: Thickness 16 â?? 300mm, width 60- 520mm Delivery condition: Hot rolled or forged Peeled or black surface, annealed or no heat treatment. Properties: A medium carbon steel is used when greater strength and hardness is desired than in the â??as rolledâ?� condition. Extreme size accuracy, straightness and concentricity combine to minimize wear in high speed applications. Turned ground and polished. pplications: Component parts for vehicles, shafts, bushings, crankshafts, connecting rods and parts for the machine building industry and steel for axes, knives, hammers etc. Heat Treatment: Soft annealing: heat to 650-700°C, cool slowly. Hardness after annealing: Max. 207 HB Hardening: 820 - 850 °C Normalizing temperature: 840-870°C Hardness after tempering: aisi 1045 steel,sae 1045 material
Product nameGalvanized steel pipe Out diameter2/1'' or 8 Wall thickness1.4mm-6mm or as per your requirement Zn coating mass480g-500g/m2 Quality gradeFirst grade Tolerance of od¡à0.3mm Length1m-6m or as per your demands Moq50 metric ton Deliver time5-15 days after receive your deposits. PackageOur products can be packed in bulk, or pvc bag; we also can package As customers requirements Payment termsT/t, l/c or further negotiation ApplicationConstruction foundation piles, steel structure building, For low-pressure fluid service. OthersWe can do special orders as customers requests! We could provide all kinds of steel pipes. Sincerely welcomes foreign and domestic customers coming throughout The business negotiations. Galvanized steel pipe is a product which is extensively used in the delivery of water, petroleum, gas .Etc. For low pressure. With high yield strength ability and good tensile ability, steel pipe is also widely used in construction, petroleum .Etc. In general, the od of the steel pipe we offered is from 1/2'' to 8'', the thickness is from 1.4 to 6.0, the length is 6m. Other sizes are also available. Besides, our steel pipe has gone through the hydraulic test and bending test or flattening test, yield strength experience , tensile stength ability .Etc. Depending on a good management system and and advanced detection system, we could guarantee the quality. Our company have got through iso9000:2008, iso9001:2008, iso14001-2004, ohsas18001-2007. Besides, we also got through the recognition of america petroleum institute, and got the certificate of api5l. With huge stock ability, we could supply you the quickest delivery. With a strict quality control system, we could supply you low price but guarantee the quality. Export standard packaging or in bulk, in woven bags or as per your demands
Product Name Seamless Carton Steel Pipe Grade Q235 = S235 / A53 Grade B / A500 Grade A / STK400 / SS400 / ST422 Q345 = S355JR / A500 Grade B Grade C Q355,45#ï¼?40# Length 5.8~12.0 m or as customized Surface Treatment Prime quality (bared, oiled, color paint, 3LPE, or other anti-corrosive treatment) Inspection With Chemical Composition and Mechanical Properties AnalysisDimensional and Visual Inspection, also with Nondestructive Inspection.
Supplier: Carton steel
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder