Silicone Potting

Specifications of silicone potting : Two parts silicone , applicable to sealing , bonding, coating for electronic parts. n be used for a long time under the temperature of -60c ~200 c with the characteristic of moisture-proof and waterproof, radiation-proof as well as weatherable and anti-ageing. 2. No significant exothermal or shrinkage during curing. 3. Very stable to changes of temperature, stability over wide temperature range (-50 to 200 oc). For getting further information about silicone rubber for potting, pls contact with miss sara

Product Feature of Electronic Potting Silicone Rubber HY-9055 silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)PP ABS PVC, etc. and metal materials. 2. Typical Application of Electronic Potting Silicone Rubber HY-9055 electronic potting silicone rubber could be applied to - high powered electronics, - DC/DC module and circuit board which requires heat dissipation and high temperature resistance. -It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. 3. Technical Guidelines of of Electronic Potting Silicone Rubber a, Pls put part A and part B in separate container and stir evenly before mixing the two part together. b, Mixing Ratio: part A: part B = 1:1 c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring. Note: The thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80?100?, the silicone will cure in 15 minutes; while in 25? room temperature, the silicone will cure around 8 hours.

There are many kinds of Encapsulating silicone rubber. Different kinds of potting silicone have great differences in temperature resistance, waterproofing, insulation, optical properties, adhesion properties of different materials and softness and hardness. Hong Ye Jie only produce and provide rtv2 silicone rubber for electronic potting, which is consist of two parts, part A and B. Which will vulcanize in room temperature or heated temperature.

electronic potting silicon Rubber Characteristics 1. No toxicity, solventless, no odor or cure by-product. 2.No significant exotherm or shrinkage during curing. 3.Flexible curing schedule, can be cured at room temperature (R.T.) or at elevated temperature. 4.Very stable to changes of temperature, stability over wide temperature range (-50 to 200 C). 5.Good thermal conductivity. 6.Excellent dielectric properties for maintaining and protection of existing electrical insulation requirements. 7.Excellent weather resistance and waterproof property for protection from moisture and dust contamination. 8.Relative easier removal benefits to repair of electrical/electronic devices 9.Green environmental protection. Applicationof electronic potting silicon Rubber - high powered electronics - LED, LCD electronic display - circuit board - PCB substrate,etc - Precision Electronic Components, - DC/DC module and circuit board protection which requires high transparency and recovery. electronic potting silicon Rubber Warm Tips 1. The electronic potting silicon rubber should be sealed storage.The mixture should be used up at once, avoid causing waste. 2. The electronic potting silicon rubber belongs to non-dangerous goods, but keep away from mouth and eyes. 3. When electronic potting silicon rubber gets stratified after a period of storage, Please mix the electronic potting silicon rubber evenly before using, it does not affect the performance

Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã??PPã??ABSã??PVC, etc. and metal materials. 2. Typical Application of Electronic Potting Silicone Rubber HY-9055 electronic potting silicone rubber could be applied to - high powered electronics, - DC/DC module and circuit board which requires heat dissipation and high temperature resistance. -It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.

1. Product Feature of Electronic Potting Silicone Rubber Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)PPABSPVC, etc. and metal materials. 2. Typical Application of Electronic Potting Silicone Rubber HY-9055 electronic potting silicone rubber could be applied to - high powered electronics, - DC/DC module and circuit board which requires heat dissipation and high temperature resistance. -It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. 3. Technical Guidelines of of Electronic Potting Silicone Rubber a, Pls put part A and part B in separate container and stir evenly before mixing the two part together. b, Mixing Ratio: part A: part B = 1:1 c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring. Note: The thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80ï½?100, the silicone will cure in 15 minutes; while in 25 room temperature, the silicone will cure around 8 hours. 4.Notes of Electronic Potting Silicone Rubber a.The following material may hinder the curing of HY-9055, So pls use after the test. When necessary, pls clean the application areas. Organotin compound or Condensation silicone with organotin Sulphur, sulfide and sulfur rubber materials. Amine compounds as well as contains the amine materials. Pewters solder flux b. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste. c. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes. d. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance

Electronic potting compound silicone Technical guidelines of electronic potting silicon rubber 1, please put part a and part b in separate container and stir evenly before mixing the two part together. 2, weight ratio: part a: part b = 1:1 3, deaeration the mixture under 0.08 m pa for 3 minutes. 4, the temperature influences the curing time of 9355 electronic potting silicon rubber. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. Warm tips of electronic potting silicon rubber: 1.The following material may hinder the curing of the product.So please apply after summary experiment. When necessary, please clean the application areas. Condensation silicone which not completely cured or organic tin compounds Sulfur, sulfide and sulfur rubber materials. Amine compounds as well as contains the amine materials. Pewters solder flux. 2. Should be sealed storage.The mixture should be used up at once, avoid causing waste. 3. Electronic potting silicon rubber belongs to non-dangerous goods, but keep away from mouth and eyes. 4. When electronic potting silicon rubber gets stratified after a period of storage, please mix 9301 evenly before using, it does not affect the performance. 20kgs/drum, 25kgs/drum, 200kgs/drum

;Key Features .Two-part : mixture addition type silicone adhesive 2.Low hardening shrinkage 3.Excellent electrical insulation in high temperature and stability 4.Good waterproof and moisture resistance 5.Excellent flame resistance, UL No: E34099 ;Typical Applications Used for encapsulation of various modules, automotive module, LED Power driver modules, Solar panel junction box, EV charging column module, Lithium battery pack, Capacitor banks, Magnetic induction coils, Power inverters, etc. ;Technical Data Table PROPERTY STANDARD/UNITS VALUE of SI2230 ---- ---- PART A PART B Color Visual inspection white / black viscous liquid white viscous liquid Viscosity 27;C, cps 6;¨¤500 6;¨¤500 Density 27;C, g/cm3#6;¨¤0.05#6;¨¤0.05 Mixture ratio Mass ratio A:B=00:00 Viscosity of mixture 27;C, cps 6;¨¤500 Operation time 27;C, min 60¨¤0 Cure condition RTV/HEAT 27;C/ 4 hour;#7;C/ 30min Cured appearance ---- White/ Gray-black elastomer Hardness Shore A 56;¨¤5 Thermal conductivity W/mK 0.80 Linear expansion coefficient K-, ppm 300 Dielectric strength kV/mm, 27;C Y20 Volume resistance DC500V, ohm-cm .¨¢05 Loss factor MHz 0.009 Dielectric constant MHz 3.00 Application temperature C -60~200 Flame resistance UL-94 V-0 Part A--0 KG/Bucket, Part B--0 KG/ Bucket.

ZS-GF-5299E is a low viscosity two-component addition cure silicone sealant, that can be cured at room temperature or heat cure, the higher the temperature, the faster the curing. This product does not produce any byproducts in the curing reaction, which can be applied for PC (poly-carbonate), PP, ABS, PVC and other surface of metal. Complied with the ROHS, REACH of EU directive.