Product: hot briquetted iron (hbi) chemical fe(total):92.5% min. Fe(metallic):85.0% min. Carbon:1.2% +/- 0.3 , phosphorus:0.040% max. Sulphur:0.015% max. Physical bulk density:2.4 - 2.7 mt/m3 nominal size:110mm x 50mm x 30mm, size distribution: +4mm to 200mm:95% min. -4mm:5% max.
Loose in bulk / containers (20').
HBI is a briquetted form of direct reduced iron with a high iron content (>90%). The chemical composition of the HBI we supply is consistent, with low levels of harmful impurities, such as phosphorus and sulphur. It is free from other harmful elements, such as copper, nickel, and any non-metallic compounds.
HBI is the preferred DRI product for the merchant metallic market; Because it is much denser than CDRI, which reduces the re-oxidation rate. In fact this enables HBI to be stored and transported without special precautions under the International Maritime Organization (IMO) code for shipping solid bulk cargoes. Besides we can use it the EAF, BF, and BOF. Consequently, HBI which is the product of compressing DRI discharged from the MIDRE Shaft Furnace at 650 C into pillow-shaped briquettes; with a typical size of 30 x 50 x 110 mm and a density 5 gm/cc. No binder is used to make HBI.
Hot Briquetted Iron ( HBI ) are for sale in both containers and in Bulk. Those who have interest can contact us.
Hot Briquetted Iron (HBI) is a relatively new product, developed in the past 25 years, as a supplement for pig iron and scrap in electric furnace steel mills. It is a compacted form of direct reduced iron (DRI), which facilitates its handling, storage, and use Origins: Iran
Dear Sir/ Madam, We are pleased to offer you Hot Briquetted Iron Chips with Libyan origin. Below is the Chemical composition: CHEMICAL COMPOSITION: Iron (Fe) - 86% min Alumina (Al2O3) - 2.5 max Silica (SiO2) - 3.5 max Phosphorus (P) - 0.08 max Sulphur (S) - 0.08 max PHYSICAL SIZE (On Natural Basis) 6.5mm - 14mm: 70% min 14mm - 16mm: 20% max 16mm - 18mm: 10% max Analysis report is available upon request. Please let us know any interest. Thanks & Best Reagrds, Maria Lorena C. Sioson
Analysis: Item Test Method Weight Average results(%) Fe total ASTM E246 87.90 Fe metal ISO 5416 79 metallization --- 89.90 C ISO 9686 0.62 S ISO 9686 0.011 AL2O3 ASTM E1621-05/ISO 12677-03 0.73 CaO ASTM E1621-05/ISO 12677-03 0.73 MgO ASTM E1621-05/ISO 12677-03 2.36 P ASTM E1621-05/ISO 9516 0.015 SiO2 ASTM E 1621-05/ISO 9516 2.890
Because of the bright future of the universal requirement for DRI briquette over the next two decades, a new method was created in 2009 in Iran to produce a cold briquette of CDRI (Patent No. IR60923). Cold-Briquetted Sponge Iron (CBSI) was the name given to the new product. Afterward, following pilot-scale and performing various laboratory studies, Cold-Briquetted Iron and Carbon (CBIC) was invented in Iran as a premium product over CBSI because of the prior�¢??s higher carbon content sand higher efficiency through processes of steelmaking (Patent No. IR84090). Owing to the fact that the cold-briquetting process of DRI is being done under high pressures, the density and mechanical strength of CBIC should be higher and the surface area and also porosity should be less than DRI�¢??s. thus, the oxidation rate, dust and fine generation rate, and the moisture adsorption capacity of DRI will considerably decrease through the process of cold briquetting. These improvements would have big technical, economic and environmental effects on direct reduction and industries steel manufacturing and will push them heading for more sustainability
Supplier: Hot Briquetted Iron
Supplier: Hot briquetted iron, hrc
