The pad printing silicon rubber usages:
The silicon rubber is mainly use for printing irregular patterns of plastic toys, electroplating toys, trade makers .Silicon pad printing is a carrier which transfer printing the patterns on the steel plate onto the toys products surface.
Pad printing silicon rubber features:
Pad printing silicon rubber with high print times and abrasion resistance, without any inpurities, with good printing effects, permanent and durable, we can provide all kinds of colors are available and our catalyst is free charged.
Pad printing silicon rubber operation instructions:
Pad printing silicon rubber is two-component silicone, part a is the liquid silicon rubber, part b is the catalyst. The usual mxing ratio for silicone rubber and catalyst is 100 : 2-3, eg. We take 100grams of liquid silicon rubber, then we add 2-3 grams catalyst, mix then evenly and pour it to your mold. Then after 2-4 hours, you will obtain a printing pad.
Frequently asked question of pad printing silicon rubber:
The reasons why the silicon pad has a short service life are listed as follows:
(1)the problem caused by inappropriate filtration of silicone rubber, and impurities in the packaging process due to the uncleanness of barrels and bags.
(2)the short service life of the silicone pad has a close relationship with the adding amount of silicone oil. The more the silicone oil added, the softer the silicone pad will be. The silicone oil will destroy the molecule of the silicone rubber, thereby bringing about the non-durable and easy ageing of the silicone pad.
Manual mold silicone rubber application This product is mainly applied in manual mold design, PVC plastic mould, cement product mould, melting-point alloy mould, alloy toy craftsworks, plastic toy craftwork, gift and stationery, big statue, cultural relic duplication, shoe sole mould production, pad printing orientation, electronic appliances vibration resistance, etc. Manual mold silicone rubber description This product with temperature and deformation resistance as well as low contraction ration, it also offer quick copying with precise contraction ration (up to two thousandth) for mold making. Is mainly applied in manual mold design, PVC plastic mould, cement product mould, melting-point alloy mould, alloy toy crafts, plastic toy, craftwork, gift and stationery, big statue, cultural relic duplication, shoe sole mould production, pad printing orientation, electronic appliances vibration resistance. 25kg/drum, 200kg/drum.
Introduction of rtv 2 molding silicone rubber: 1. Two-part of rtv 2 molding silicone rubber: flowable liquid silicon and catalyst. 2. Rtv 2 molding silicone rubber cures at room temperature within 4-6 hours. Features of rtv 2 molding silicone rubber: 1. Rtv 2 molding siliconerubber has an exceptional fluidity and good operability. 2. Rtv 2 molding silicone rubber hasgood temperature and deformation resistance as well as low shrinkage. 3. Rtv 2 molding siliconerubber has high duplication times. Operation step for rtv 2 molding silicone rubber: 1. Step one to use rtv 2molding silicone rubber: take 100g of part a and add 2g of part b and mix thesilicon rubber and the curing agent evenly. 2. Step two to use rtv 2molding silicone rubber: vacuum pumping 3. Without exception, thistakes less than 10 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available. 4. Step three to use rtv 2molding silicone rubber: brushing cast & perfusion molding operation. 25kgs/drum vacuum package or 200kgs/drum
Supplier: Engineering goods like machined, forged, stamped, casting, aluminum casting, aluminum extrusion, fasteners, springs, washers, gaskets, oil seals, rubber components, etc
Name: Rubber band Size: Can be customized Sample lead time: 3~5 working days MOQ: 300kgs Product Features: 1. High Toughness,Good elastic ,Can Be Extended To Seven Times Length Won't Break 2. Environmentally Friendly,Nontoxic ,Anti-aging,Not Stickly! 3. Vietnam Import Natural Rubber ,100% Rubber Content ,Quality Guarantee Standard packing: 100grams/polybag, 200grams/polybag, 300grams/polybag, 30kg/bag,etcâ?¦.or depending on needs of customer. Production lead time: 3 days by store in warehouse and 10-15 working days according to customerâ??s Color and SIZE .(depend on the order quantity)
Natural Rubber SVR3L have good resilience, abrasion and surface friction properties and excellent compression set. It has low hysteresis and rolling resistance with high fatigue resistance and remains flexible at low temperatures. Natural rubber SVR3L has poor resistance to oil, sunlight and ozone and limited thermal capability. Natural rubber SVR3L is superior tear strength and excellent resistance to heat buildup continues to make it a favored ingredient for high-performance tires for race cars, trucks, buses and aircraft. Other applications include tank lining, engine mounts, seals, vibration dampening and diaphragms.