Silicone Rubber For Molding

Model530 Colorwhite Mixing ratio (%)2% Pot life (mins, under 2530-40 Curing time(hrs, under 25)3-4 Hardness  ( shore a )30±2 Tensile-strength  (mpa)4.2 Tear-strength (kn/m)26±2 Viscosityafter a/b mixed , mpa.S27000±2000 Shrinkage rate (%0.2% Elongation450

Various properties about excellent liquidity, good work-ability, good tensile?force, with no deformation, heat resistant, acid and alkali resistant. Can be used repetitively. 2.Specification Silica gel is mixed with curing agent, the appearance of molding silica gel is liquid, A substitutes silica gel, B substitutes curing agent. For example, 100g A add 2g curing agent, but it needs to note, A and B must be mixed averagely, if not, the molding will not cure completely, and heterogeneous silica gel can affect its life time and result in that the molding will be completely scrapped. Packaging by airtight polyethylene drum.

1.Description of liquid silicone rubber C830 Silicone rubber is condensation cure silicone rubber for mold making. The silicone rubber will be cured under room temperature, It’s two-components, the mixing ratio is 100:2 . Part A is a flowable liquid silicone , part B is the catalyst. It has an exceptional fluidity and good operability. C-830 tin cure mold silicone has a good property , it is suitable for various mold making . 2.Characteristics of liquid silicone rubber *An exceptional fluidity and good operability, easy to demold *Good tensile strength and tear strength *lower shrinkage *non-deformation ,non-oily *good flexibility *eco-friendly *long shelf-time &lifetime 3.Application of liquid silicone rubber stone mold ,concrete mold , cement casting mold polyurethane casting mold , GRC casting mold , fiberglass cating mold statue mold , sculpture mold , resin craft mold ,artificial wooden mold gypsum mold , plaster mold ,bronze casting mold candle mold ,soap mold, shoe mold , tyre mold ,etc ..... C830 Silicone rubber is mainly suitable middle sized product and big size with simple pattern. Package: 1kg/drum,5kgs/drum,20kgs/drum,25kgs/drum,200kgs/drum based on vacuum packing. Shelf life and transportation 1. Twelve(12) months when stored at 25C in tightly closed original packages. 2. This kind of product is non-dangerous product, which could be transported as general chemicals.

1. Description of rtv 2 liquid silicone rubber for frame gypsum molds C830 silicone rubber is condensation cure silicone rubber (tin cure silicone rubber) for mold making. The silicone rubber will be cured under room temperature. It's two components, the mixing ratio is 100:2. Part A is a flowable liquid silicone, part B is the catalyst. It has an exceptional fluidity and good operability. 2. Characteristics of rtv 2 liquid silicone rubber for frame gypsum molds * An exceptional fluidity and good operability, easy to demold * Good tensile strength and tear strength * Suitable hardness * Copy detailed pattern * Good flexibility * Eco-friendly * Long shelf-time &lifetime 3. Application of rtv 2 liquid silicone rubber for frame gypsum mold C830 liquid silicone rubber is perfect molding material, it is suitable to make mold for concrete casting, artificial stone, brick, cement casting, gypsum decorations, plastic product, resin craft, polyester, polyurethane, bronze casting, statues, jewelry, wax, crystal, tire mold, shoe mold, clay casting, ceramic casting. etc. C830 liquid silicone rubber is mainly suitable for small or middle sized products with delicate pattern by pouring and brushing operation. Package 1kg/drum,5kgs/drum,20kgs/drum,25kgs/drum,200kgs/drum. Shelf life and transportation 1. Twelve(12) months when stored at 25C in tightly closed original packages. 2. This kind of product is non-dangerous product, which could be transported as general chemicals.

Liquid RTV Molding Silicone Rubber raw material for all kinds of mold making Features of liquid RTV Molding Silicone Rubber raw material for all kinds of mold making: 1. Two part of liquid fluid: liquid white silicone and curing agent. 2. Cure at room-temperature within 4-8 hours, but all performance will act perfectly when it cure within 2 - 4 hours. 3. Good fluidity and excellent operation. 4. Good resistance to weather, temperature, aging, acid. 5. Excellent tear strength, comfortable duplication times. Application of liquid RTV Molding Silicone Rubber raw material for all kinds of mold making: 1.Resin crafts, unsaturated resin crafts 2. Poly resin crafts, candle crafts, plastic crafts 3. Making molds forgypsum,GRC,concrete,Artificial stone products molding,Wax casting 4.Decoration building mold making 5.Lighting & candles crafts,stationery gifts,crafts industry 6.Casting for Statue,Buddha, Christmas ornaments,sculptures, figures etc Operation Instruction for Liquid RTV Molding Silicone Rubber raw material for all kinds of mold making : RTV-2 liquid mold silicone rubber is a kind of flowing liquid, and it consists of two component, part a is a flow-able liquid silicone rubber, part B is the curing agent. 1. Firstly, after your previous work of dealing with the original model, take some liquid silicone rubber, add 2%~3% cuing agent of the amount of silicon and mix themevenly. 2. Then after vacuum-pumping the mixture, you can pour it into the mold frame. 3. The silicone mold will cured in 2~3 hours. Note: the time for vacuum-pumping should be less than 3-5mins, otherwise, once the silicone rubber has cross-link reaction during vacuum. it will not be operated.

1. Description YJS-620 is a two-component 1:1 Mix addition (platinum)cured RTV silicone rubber which cures at room temperature. Because of its considerable fluidity, it is recommended for the duplication of models with many undercuts. This stuff is really thin and easy to pour.    2. Features *high chemical resistance to the aggressive components of some types of resin *High resistance to laceration (this characteristic guarantees high resistance to wear and tear) *High level of accuracy in reproducing very small particulars *High dimensional stability over time and non-deformability *Considerable resistance to high temperatures and to ageing *Excellent non-stick effect *Soft, stretchy, high tear resistance, *Will not shrink in service

1.Description of Platinum liquid silicone rubber for mold making G830 Silicone rubber platinum cure silicone rubber. The silicone rubber will be cured under room temperature and can be cured fast by heating, It’s two-components liquid silicone rubber , the mixing ratio is 1:1 . It has an exceptional fluidity and good operability.Especially ,the platinum cure silicone rubber has a lower shrinkage,higher temperature resistance and it is flexible. 2.Characteristics of Platinum liquid silicone rubber for mold making *An exceptional fluidity and good operability *Good tensile strength and tear strength *Food grade silicone rubber *high temperature resistance *good flexibility *No smell ,non-toxic *long shelf-time &lifetime *Lower shrinkage 3.Application of Platinum liquid silicone rubber for mold making G830 silicone rubber is flexible silicone rubber ,it has a higher temperature resistance and lower shrinkage, so it is suitable to make the silicone gasket for machine sealing . 4.Datesheet of Platinum liquid silicone rubber for mold making Item No. Appearance Hardness (shore A°) Viscosity (CPS) Tensile-strength( kgf /cm2 ) Tear-strength (kgf /cm2 ) Elongation-break(%) Mixing ratio operation time (25? ) Curing time( 25 ?) shrinkage G830 translucent 30±2 7000±1000 =55 =24 =450 1:1 20-30 mins 2~3 h =0.1% Packing: 20KG/drum vacuum packing for part A + 20KG/drum vacuum packing for part B 25KG/drum vacuum packing for part A + 25KG/drum vacuum packing for part B 200KG/drum packing for part A +200KG/drum packing for part B

Factory price rtv2 silicone rubber for crafts molding Crafts Molding Silicone 1.Description 2. Technical Datasheet Typical general characteristics Inspection MethodValue Product data (Catalyzed A+B)C-820C-825 HardnessShore A20±225±2 Mix RatioA:B100:3100:3 Color/WhiteWhite Pot life25 °C (77F)30-40mins30-40mins Curing time25 °C (77F)3-4 hours3-4 hours Mixed viscositymPa.s16000±100020000±1000 Tear-strengthkg/cm20±222±2 Tensile-strengthM.pa3.6±0.54.0±0.5 Elongation%400±50450±50 Shrinkage%?¤0.3?¤0.3 Note: This is a 100A:3B mix ratio product that must be measured by weight. The choosing of suitable hardness should be according to the size and pattern design of the products. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise. 3. FEATURES Low viscosity,great flexibility,Extra low shrinkage,Chemical resistance,release properties, Easy to work with,High tear strength,Heat Resistance,various color is available,High reproduction rate 4.SHELF LIFE: When stored at or below 32°C (89.6°F) in the original unopened containers, C-8 series Silicone Base and its Curing Agents have a usable life of I0 months. 5.Package Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum. Curing Agent: 30g/bottle; 1kg/bottle

1) Applications: OTT mold making liquid silicone rubber for plaster mold is primarily intended for poly resin crafts, PU crafts, PU resin crafts, gypsum crafts, unsaturated resin crafts, lighting and candles crafts , plastic toy, stationery gifts crafts industry, a large statue Buddha, relief, furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, large-scale cement mold, artificial fossils Factory, Europe componentfactory, simulation landscapes, animals and plants sculpture, sandstone crafts and so on. 2) Description: OTT mold making liquid silicone rubber for plaster mold is white or red flowing liquid with general hardness of 22-50A after curing. Molding silicone is a kind elastic silicone which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tears strength and elongation.