Designation by standards Brand name din en aisi Better s2-10-1-8hs2-9-1-8m42 Chemical composition (in weight %) C si mn cr mo niv w others 1.10max. 0.70max. 0.404.009.50-1.101.55co: 8.00 Description Capable of very high hardness values, this is a moly type high speed tool steel. The alloy has excellent hot hardness and wear resistance and is commonly employed to machine difficult to machine materials including the superalloys. Applications Typically employed to machine the superalloys and exotic, m42 is employed in drills, hobs, taps, end mills, milling cutters, form and gear cutters, broaches and chasers. Physical properties (avarage values) at ambient temperature Density [g/cm3]: 8.01 Thermal conductivity [w/m.K]: 19.0 Coefficient of linear thermal expansion 10-6 oc-1 20-100oc20-200oc20-300oc20-400oc20-500oc20-600oc20-700oc20-800oc 9.810.811.111.611.912.212.512.6 Soft annealing Heat to 820-880oc, cool slowly in furnace. This will produce a maximum brinell hardness of 230-300. Stress relieving Stress relieving to remove machining stresses should be carried out by heating to 650oc, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment. Hardening Heat up to 450-600oc, then preheat to 850oc, and to 1050oc. Harden from a temperature of 1160-1210oc followed by oil, air quenching or warm bath 550oc. Hardness after quenching is 66-68 hrc. Transformation temperatures: ac1=780oc , ac3=855oc. Tempering temperature (oc) vs. Hardness (hrc) 200oc300oc400oc500oc520oc540oc560oc580oc600oc650oc700oc 62.56161.566.568686765.5645042 Tempering diagram Click the image to enlarge the diagram.Forging Hot forming temperature: 1095-982oc. Machinability Rated at 45% of a 1% carbon steel, the alloy, in its annealed condition, can be turned, drilled, tapped, milled, broached and threaded.
High speed steel W6Mo5Cr4V2 Anneal temperature: 840-860oC Relief annealing temperature: 720-760oC Hardening temperature: 1210-1230oC Hardening medium: salt bath under 600oC,aslo use oil cooling or air cooling Normal temper temperation: 540-560oC RC Rockwell Hardness after hardening and temper: 63-66 Characteristic:Tungsten-molybdenum high speed steel developed by China, high performance in toughness, hardness, high temperature hardness. Application: Can be used in the manufacture of high capacity cutting tools to bear impact force ,such as gear shaper cutter, milling cutter,screw tap,drill bit etc.Also can be used in manufacture of large scale and thermoplasticity shaped cutting tools and antiabrasive cutting tools under high load.
High speed tool steel is mainly used for the manufacture of high efficiency. In the annealed state, the main alloying elements in high speed tool steel are tungsten, molybdenum, chromium, vanadium.Because of its high red hardness, good abrasion resistance, high strength characteristics, also used in the manufacture of tool knive and saw blades
Features 1.Similar to M2 high speed steel. 2.Add cobalt to increase hot hardness. 3.Offers excellent cutting performance. Shape:steel plate/flat bar/round bar Technology:Hot work / Forged/cold drawn Heat treatment:Annealed / Q+T Surface condition:Black/Peeling/Polishing/Machined Delivery condition:Hot rolled or forged, Peeled or black surface Test:UT 100% / SGS Certification:ISO/mill certificate
Fe 78% W 5.5% Mo 5.5% 15% humidity Approx. 50tm
1. High speed steelM2 2. Forged or hot rolled 3. Fast cutting steel with high resistance 4. High hardness 5. EAF+LF+VD+ESR Technogoly:EAF+LF+VD+ESR Trade patterns:CIF and FOB Shape:round bars and flat bars 1. M2 is a general purpose high speed steel. M2 high speed steel offers good wear resistance with excellent toughness and cutting power. 2. Chemical composition :(%) C:0.80~0.90; Si: 0.40; Mn: 0.40; W: 5.50~6.75; Mo:4.50~5.50; Cr:3.80~4.40; V:1.75~2.20, S:0.030 P:0.030 3.Forging: The forging temperature for high speed steels is 1050¡ã/1150¡ãC. Do not charge direct into the high temperature part of the furnace, but pre-heat slowly to 850¡ã/900. During the forging, the temperature of the material drops below 880/900¡ãC, reheating will be necessary. Cool very slowly after forging. 4.Features : 1) excellent ductility and abrasion resistance 2) well distribution of carbide and thermal plasticity 3) high hardness and high temperature hardness 5.Applications : For making all sorts of general tools, forming tool, and also some components, such as cold extruding dies, etc. 6.Steel Grade: GB:W6Mo5Cr4V2 AISI:M2 DIN:1.3343 JIS:SKH9 7.Mechanical Property Annealed Hardness: HB255 Quenching Hardness: HRC¡Ý63 8.Delivery Condition Forged + Annealed + Machining (Peeled/Turned) Our main products: Plastic mould steel: 1.2311, 1.2738, P21, 1.2316, 1.2083 etc. Hot work tool steel: H11, H13 etc. Cold word tool steel: O1, D2, D3, D6 etc High speed steel: M2, M35, M42 etc. Carbon steel: AISI1045, AISE1050, Q235, SS400 etc. As per standard exporting.
High Speed Steels are high performance special steels offering high hardness at temperatures up to 500 and high wear resistance, SMC high-speed steel is all produced with electro-slag refining (ESR), its grade and variety have been forming a complete range after consistently improved and its quality has reached an international advanced level. SMC Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might otherwise be caused during storage or transportation. In general we provide the packing list to our honored clients for the product packing detail, and labeled with SMC shipping mark on the surface of each package. If you have special requirement for the packing, please feel free to contact us.
1.Size of t1 alloy steel Diameter(mm):20~600 length (mm):1000~6000 Plate Thickness(mm):max:800 width (mm):max:2200 length (mm):max:6000 The specification can be customized. 2.Chemical compositions C:0.70-0.80 si:0.20-0.40 mn:0.10-0.40 p:max 0.030 s:max 0.030 cr:3.80-4.40 mo: max 0.30 w:17.50-19.00 v:1.00-1.40 3.Similar grade Gb:w18cr4v aisi:t1 din:1.3355 jis:skh2 4.Feature of t1 steel (1)tungsten molybdenum high speed steel. (2)high toughness combined with good cutting powers. (3)high hardness and wear resistance. 5.Application For cutting tools, cold forging die, wear resistance screws and cold forming tools 6.Min.Order quantity:5 ton/tons our moq is flexible Supply capacity:5000 ton/tons per month Or based on the clients' demand Port:shenzhen Payment terms:l/c, d/p, t/t 7.Packaging & delivery In seaworthy packingï¼? 20ft:gw 28t; (5.80m*2.13m*2.18m); 40ft:gw28t; (11.8m*2.13m*2.18m) or based on your order Shipped in 15 days after payment 8.Special use:mold steel 9.Surface treatment:black/polished/machined Technology:hot rolled/forged/cold drawn Heat treatment:annealing/q+t
high-speed tool steel manufacturers-Dalian Yongbao New Material Technology Co., Ltd founded in1999, it covers an area of 20,000m², construction area is 12,000m², a private enterprise which set smelting, electroslag remelting, forging, steel rolling. Our company produces high speed tool steel, die steel, stainless steel, precision alloy, high temperature alloy, corrosion resistant alloy, welding strip, welding wire, ingot, forging, hot rolled material, cold drawn material and cobalt series (M42, M35, etc.) tungsten series (W18, W6, W9, W4, M2Al, etc.) die steel (4Cr5MoSiV1-H13Cr12M1V1, CR) 12MOV, etc.) we developed various special shaped products of HSS, widely used in sawing products, high-end wood planer blades, automotive blades, air conditioning sliders, sewing machine blades and other fields, has grown into our core products. China tool steel, China high speed steel. The company has 12 product invention patents, 4 utility model patents, 9 mold steel, tool steel production line software copyright patents, and passed the ISO-9001 international system certification in 2009.