Chlorinated Paraffin #52

1.Technical Index Appearance Chlorine Content (%) Specific Gravity D420 Acid Value (mgKOH/g) Hot Decomposition Temperature (C) White or Light yellow transparent sticky liquid 50~54 1.25 0.08 120 2.Application (1) This product is of assistant flame retardant plasticizer of PVC products, with good volatility and electric performance, making more brightness and tensile strength to the products. (2) Additive to plastic and painting products against aging. (3) Applied widely for Pvc resin, chloridized rubber, and compound paint, adhesive and ink products with stable chemical performance, against water, firing or corrosion. 250kg/galvanized iron drum, 20 metric ton per 20'container.

Supplier: Hydrogen peroxide (50%), chlorinated paraffin wax (52%), liquid chlorine

We are a leading supplier of electroplating chemicals, industrial polishing and welding consumables, water treatment, powder coating, fertilizers. We stock and carry an extensive range of ready to use chemicals. We deal with so many different chemicals and we would like you to contact us for more information about our different chemicals and products.

Chlorinated Paraffin-70 1)Technical Index Appearance:White or light yellow powder Chlorine contentú¿%ú¬:68-72 Softening pointú¿íµú¬í¦95 Hot stability indexí_ú¿%ú¬0.2 Heating lossí_ú¿%ú¬1.0 Screened residual(20 mesh)í_ú¿%ú¬0.02 2)Application ú¿1ú¬ Flame retardant for macromolecule polymer ú¿2ú¬Surface treatment agent for knitted and packing materials. internal plastic with knitted exterior covered with film, with the net weight of 25kg

Active Aluminum Hydroxide 2)Technical Index Appearance:White powder Al2O3í¦(%) :64 Firing lossí_(%) 35 Attached waterí_(%)0.5 Fe2O3í_(%) 0.03 SiO2í_(%) 0.04 Na2Oí_(%) 0.5 Activationí¦(%)98 Whitenessí¦(%)96 Physical feature: there are mainly 4 sizes of active aluminum hydroxide 3) Application: The product is made of high quality raw materials via being broken with extra micro air and surface activation of coupling agent. It is of additive smoke and flame retardant without halogen, with the features of large amount usage, good flame resistance and low cost, improving electric arc resistance, and the strength of impact and bending, being mainly applied at electric wire, cable, insulated materials, flame retardant rubber hose, tape, wind tube cloth, electric materials, etc. internal plastic with knitted exterior covered with film, with the net weight of 25kg

Antimony Trioxide (also called: antimony oxide, and antimony white informally) Molecular formula: Sb2O3 Molecular weight: 291.5 1) Technical index: Chemical Composition and Physical Performance of Antimony Trioxide Brand Name: Sb2O399.80 Sb2O399.50 Chemical Composition% Sb2O3not less than 99.80 99.5 Impurity not more than As2O3 0.05 0.06 PbO 0.08 0.10 Fe2O3 0.005 0.006 CuO 0.002 0.002 Se 0.004 0.005 Physical Performance Whiteness is not less than % 95 93 Granularity at average(um) 0.3-0.9 0.9-1.6 1.6-2.5 0.3-0.9 0.9-1.6 1.6-2.5 2)Application Antimony trioxide was one of the items firstly applied as inorganic flame retardant, being mixed with halogen compound as assistant object, with retardant role in the heat decomposition process, replacing the halogen compound partially, being applied at the sectors of plastic, rubber, chemical fiber, enamel, pigment, paint, glass, electron, etc. Internal plastic with knitted exterior covered with film, with the net weight of 25kg .

Aluminum Hydroxide Molecular formula: ALú¿OHú¬3 or AL2O3•3H2O Molecular weight: 78 1)Technical Index Chemical composition, % AL2O3 not less than Firing loss not less than Impurity not larger than SiO2 Fe2O3 NA2O AH-1 64.5 35 0.02 0.02 0.4 AH-2 64.0 35 0.04 0.03 0.5 AH-3 63.5 35 0.08 0.05 0.6 Note : 1. AL2O3 content is of the difference of 100% minus firing loss and impurity content. 2. The chemical composition is calculated of the baking at 110í+5íµ for 2 hour . 3. The impurity content is treated in line with the number rule of GB8170. Physical feature: there are mainly 4 sizes of aluminum hydroxide, 325, 800, 2,000 and 3,000 mesh. 2)Application Aluminum hydroxide is the most consumable and applicable inorganic additive flame retardant that does not only resist firing, but also prevents from smoke, dropping or toxic gas. So, it is widely used with gradual increase of the usage, at the sectors of hot solidifying and moulding plastic, synthetic rubber, coating and construction materials. internal plastic with knitted exterior covered with film, with the net weight of 25kg or 40kg

Supplier: Flame retardant:antimony trioxide, zinc borate, chlorinated paraffin-70, chlorinated paraffin-52, aluminum hydroxide, active aluminum hydroxide, decabromodiphenyl oxide, octabromodiphenyl oxide, magnesium hydroxide, active magnesium hydroxide, mpú«mp p, poly ammonium phosphate, tris(2-chloroethyl)phosphate, melamine, hexabromocyclo dodecane, tetrabromobisphenol a, decabromodiphenyl ethane, electronic sealant