Typical chemical analysis in %:H11/1.2343
Heat treament data
Temperature 800-860íµ
Duration 2-5 h
Cooling furnace
Hardness ¿Q235HBS
Soft annealing
Available size range
Round bars Dia 30-450mm
Flat bars Thickness 30-400mm Width 30-800mm
General fields of application
Tools for forging machines,dies,die inserts,extrusion tools,hot
Shearing knives and tools for plastics processing.
Similar Grade
GB 4Cr5MoSiV
AISI H11
JIS SKD61"
Specification 1.Hot work tool steel. 2.Better toughness than conventional H13. 3.Fine grain size with high toughness. 4.High strength at elevated temperature. Shape:steel plate/flat bar/round bar Technology:Hot work / Forged/cold drawn Heat treatment:Annealed / Q+T Surface condition:Black/Peeling/Polishing/Machined Delivery condition:Hot rolled or forged, Peeled or black surface Test:UT 100% / SGS Certification:ISO/mill certificate
Very good toughness in SKS sery hot roll metal steel under mediative temprerature by cold cooling hardending with rather good anti-heating and wear-resisting function; Applied in Aluminium Alloy pressure and forged moulds , Heat extrusion moulds, tools for perforating holes and other pressure forged moulds , plastics moulds , the tempering handling hardness HB
Service: Sample free Sample free and 7 x 24 hours onlie Heat treatment: Annealling or Q+T Name: 1.2343 steel Certificate: ISO/Mill Certificate / SGS Technology: Hot rolled / Forged / Cold drawn Shape: Round bars / Flat bar / plate /sheet Test: SGS /UT100%/ Elements Testing /Magentic particle Inspection Experience: More 17 years manufacturer produce experience Delivery condition: Hot rolled Or Forged / peeled or black surface / Annealing or Q+T A36 carbon mild Steel Sheet density: 7.85 Ton/ m3
H11/1.2343 tool steel is a 5% chromium hot work steel that is characterized by excellent impact toughness. It contains less vanadium than the widely-used H13 tool steel. This provides for the higher toughness, with some reduction in wear resistance and temper resistance. H11 tool steel is a deep-hardening, air-hardening steel that exhibits minimal size change during heat treatment. The steels are subjected to minimal distortion during hardening due to their balanced alloy content. It has good resistance to thermal fatigue cracking (heat checking) and excellent resistance to gross cracking and thermal shock when water cooled in service. H11 tool steel is recommended for hot tooling applications where maximum resistance to cracking is required. Such applications include hot punches, die casting dies, forging dies, hot shear blades, hot gripper dies, and extrusion tooling.
1. Hot work Tool Steel Round/Flat bar (H13/1.2344/4Cr5MoSiV1/SKD61)(Brand Product) High wear resistance, toughness and hot hardness. It is mainly used for extruding, die-castingmold and complex-shaped mold, etc. 2. Hot work Tool Steel (1.2714/L6/5CrNiMo/SKT4) It is mainly used for manufacturing hot-extrusion die, swage hammers, etc. 3. Hot work tool steel 1.2343/ H11/SKD6/4Cr5MoSiV High thermal strength, hardness, wear-resistance and toughness.It is mainly used for tools forextrusion; molds for plastics; tools for cold punching and hot sharing. flat/round bar
Innovative technology of pre-materials suitable for gas springs welded and drawn according to ASTM A213 various ID tolerance requirement of H8, H9, H10 and H11 surface roughness below 15RA (0.40 �¼m) mechanical properties are controlled to endure excessive stress hardness, tensile strength, yield strength and elongation servicing high precision pneumatic cylinder applications ODï¼?mm) ID(mm) WT(mm) ID Tolerances,+0/-0.05) Specifications Materials Surface Finish(max) 15.0 13.0 1.0 CGS-031,H9 A213 SAE1010/#10; SEA1020/#20 ;Q235; 304L;316L ID < 20 RA
Supplier: Db6, H13, H11, 2714 Steel
Supplier: Tools and alloy steels like h11 db6 wps en24 en31 en8 en19 ms en31 pipe
Buyer: Tools and alloy steels like h11 db6 wps en24 en31 en8 en19 ms en31 pipe
Supplier: Tool steel D2, D3, D6, A2, O1, O2, H13, H11, H21, P20, P20+NI, M2