Steel Grade:
DIN- 1.2714 %
C Si Mn P S Cr Mo Ni V
0,50 - 0,60 0,10 - 0,40 0,65 - 0,95 <=0,030 <=0,030 1,00 - 1,20 0,45 - 0,55 1,50 - 1,80 0,07 - 0,12
Similar Grade:SKT4
Delivery Condition :
DIN AISI
Annealed (HB) 197~241 <=250
Size available
Square/Round Bar: 70~ 550mm
Flat: Min thickness, 15mm ; max width, 1000mm
Block: Mini size,20x 50mm , max, 400x 800mm
Delivery Condition :
GB/T1299-2000 DIN AISI
Annealed (HB) 197~241 <=250
Size available
Square/Round Bar: 12~ 550mm
Flat: Min thickness, 15mm ; max width, 1000mm
Block: Mini size,20x 50mm , max, 400x 800mm
Delivery Condition: hot rolled,forged, annealed, black surface / ground surface / peeled surface / milled surface.
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder
High Precision Steel Pipe for Gas spring Cylinder Type:Seamless and Welded Steel Tube Roughness 0.1-0.8ra Material E195-E235,Q195-Q235,#10,#20,#45,SAE1010,SAE1020 Surface:Black/bright Standard:DIN, GB, JIS, DIN 17175, DIN 2391, GB 5310-1995, GB/T 13793-1992, GB/T 3094-2000, GB/T 8163-1999, JIS G3101 Size :OD 3mm-140mm Thickness 0.5-20mm Processing :Cold rolled /cold drawn 1. BK (+C) No heat treatment after last cold forming process. 2. BKW (+LC) After last heat treatment there is a light finishing pass (cold drawing) 3. BKS (+SR) After the final cold forming process the tubes are stress relieve annealed. 4. GBK (+A) After the final cold forming process the tubes are annealed in a controlled atmosphere. 5. NBK (+N) After the final cold forming process the tubes are annealed above the upper Woven bag / wooden or crate carton/ Bundle Packing/ Plain end or vanished as per customer's request. Usage: Gas Spring Cylinder Taian Henson Metal Co lTD