Heat Treatment
DIN 1.2379 steels alloy should be preheated very slowly to 815 (1500 F) and the temperature can be increased to 1010oC (1850 F). Then held at 1010oC (1850 F) for 20 to 45 minutes and air-cooled (air quenched).
Annealing
Annealing of 1.2379 tool steels material should be done at 871 to 898 C (1600 to 1650 F) followed by slow furnace cooling at 4.4 C (40 F) per hour or less, after which cooling rate could be increased. At the same time, must do something to prevent excessive carburization or decarburization.
Stress Relieving
Heat it slowly to 1050 -1250 F, allow to equalize, and then cool in still air(Strain Relieving)
Preheat Prior To Hardening
Preheat slowly to 1350 -1450 F and hold at this temperature until steel 1.2379 steel material is uniformly heated.
Hardening
After thorough preheating, heat to 1800 -1850 F. Hold it at the hardening temperature until it is completely and uniformly heated.
Quenching
DIN 1.2379 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization on the surface, controlled atmosphere or vacuum furnaces are recommended. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
Tempering
The tempering temperature on material 1.2379 steel may be varied according to the desired hardness. 1.2379 steels can be tempered at 204 C (400 F) for achieving Rockwell C hardness of 61 and at 537 °C (1000 F) for a Rockwell C hardness of 54.
Compare
Chinese Cr12Mo1V1 steel, American D2 steel, Japanese SKD11 steel, the chemical composition of them is the same, but the performance is very different. After heat treatment, the color of Cr12Mo1V1 is a little orange-red, and the deformation would be large. It is easy to fracture during use. And the hardness of D2 steel is higher than SKD11 steel, but the toughness is not better than SKD11 steel. SKD11 steel is light and smooth, with the best overall performance.
D2 Steel Forging
Heating for forging of AISI D2 tool steel should be done slowly and uniformly. Soak through at 1850 -1950 F and reheat as often as necessary, stopping work when the temperature drops below 1700 F(926 C). After D2 mold steel forging, cool slowly in lime, mica, dry ashes or furnace. D2 steel should always be annealed after forging.
Songshun specialized in Special Steel for almost 20 years. We can supply mold steel, high speed steel, alloy steel, free cutting steel and etc.Welcome your contact 24 hours a
Supplier: Led bulb, tube light, panel light, decoration light, wall light, steel wires, steel plate, stainless steel plate, twisted wire rods, galvanized wires, wire mesh, site fencing, mosquito mesh, thread rods, rebar, twisted rods, t bar, nuts and bolts, hardware, pvc pipes, upvc pipes, api pipes, melamine, mdf board, plywood, film faced, shuttering, packing, core veneer, face veneer, hdf molded door skin, door filler, tubular particle boards, pvc boards, wpc boards, doors, block board, hard board, gypsum board, canopy, carpet, flooring wooden, bamboo, laminated engineering, tiles, granite tiles, granite blocks, black galaxy, wash basin, water closets, washbasins, ss sinks, faucets, furniture, pvc edge bending, crew, locks, pvc seals, silicone cartridges, shower enclosures, shower door hinges, handles, knobs, brackets, slides, nails, solar panels, flexible solar panels, solar power station, battery, inverters, rechargeable fans, lights, spring, 3ply disposable face mask, oxygen concentrator ,
Services: Buying office, oem, components sourcing, value added services
Buyer: In shell pecan nut, macadamia nut
Model Number: 314 321 441 430 Type: plate Application: decoration Certification: ISO Tolerance: 1% Processing Service: Bending, Welding, Decoiling, Punching, Cutting Product name: aisi 314 321 441 430 stainless steel sheet Surface: 2B, NO.4 HL available Technique: Cold Rolled Finish Material: Stainless Steel Color: Natural Color Edge: mill Edge/ slit edge Item:ISO9001 Standard Packing: Standard Export Packing Ni:min1%
Description:Stainless Steel Sheet, Cold Rolled Stainless Steel Sheet, Hot Rolled Stainless Steel Sheet Type:201 202 304 316L 310S 309S 321 316Ti 410 420 430 409 duplex,SAF2205,S31803 Thickness: 0.3-60mm Width: 500-2000mm or customized Length: 1000-6000 or customized Standard size: 1000-2000mm, 1250-2500mm, 1219-2438mm, 1500-3000mm Surface:2B, No.1, No.4, HL, BA, 8K etc Standard: ASME, ASTM, EN ,BS,GB,DIN, JIS etc Application: Stainless steel sheet applies to construction field, ships building industry, petroleum & chemical industries,war and electricity industries, food processing and medical industry, boiler heat exchanger,machinery and hardware fields.
We deals in the following products of India, China, Taiwan and Korea Origin:- Stainless Steel Sheets
Description:Stainless Steel Sheet, Cold Rolled Stainless Steel Sheet, Hot Rolled Stainless Steel Sheet Type:201 202 304 316L 310S 309S 321 316Ti 410 420 430 409 duplex,SAF2205,S31803 Thickness:0.3-60mm Width:500-2000mm or customized Length:1000-6000 or customized Standard size:1000-2000mm, 1250-2500mm, 1219-2438mm, 1500-3000mm Surface:2B, No.1, No.4, HL, BA, 8K etc Standard: ASME, ASTM, EN ,BS,GB,DIN, JIS etc Application:Stainless steel sheet applies to construction field, ships building industry, petroleum & chemical industries,war and electricity industries, food processing and medical industry, boiler heat exchanger,machinery and hardware fields.
Description:Stainless Steel Sheet, Cold Rolled Stainless Steel Sheet, Hot Rolled Stainless Steel Sheet Type:201 202 304 316L 310S 309S 321 316Ti 410 420 430 409 duplex,SAF2205,S31803 Thickness:0.3-60mm Width:500-2000mm or customized Length:1000-6000 or customized Standard size:1000-2000mm, 1250-2500mm, 1219-2438mm, 1500-3000mm Surface:2B, No.1, No.4, HL, BA, 8K etc Standard: ASME, ASTM, EN ,BS,GB,DIN, JIS etc Application:Stainless steel sheet applies to construction field, ships building industry, petroleum & chemical industries,war and electricity industries, food processing and medical industry, boiler heat exchanger,machinery and hardware fields.
Description:Stainless Steel Sheet, Cold Rolled Stainless Steel Sheet, Hot Rolled Stainless Steel Sheet Type:201 202 304 316L 310S 309S 321 316Ti 410 420 430 409 duplex,SAF2205,S31803 Thickness:0.3-60mm Width:500-2000mm or customized Length:1000-6000 or customized Standard size:1000-2000mm, 1250-2500mm, 1219-2438mm, 1500-3000mm Surface:2B, No.1, No.4, HL, BA, 8K etc Standard: ASME, ASTM, EN ,BS,GB,DIN, JIS etc Application:Stainless steel sheet applies to construction field, ships building industry, petroleum & chemical industries,war and electricity industries, food processing and medical industry, boiler heat exchanger,machinery and hardware fields.
Supplier: Chemical, chemical raw material, auxiliaries, solvents, paint, textile fiber, rubber, plastic, paint drier, plasticizer, flame retardant, surfactant, additives, steel pipe, steel tube, stainless steel tube, stainless steel pipe, ms pipe, pipe fitting, flange, fasteners, steel wire
Services: Transportation agent,customs clearance service,
Buyer: Import chemical raw materials, auxiliaries, bulk commodities
Supplier: Hr coil/sheets/plates, crca coil/sheets, gi coil/sheets, hrpo coil/sheets/plates, ms angle, ms channel, ms wire rod, ms universal column, ms universal beam, ms flat, ms rounds