JC CURE ZBP non Staining nitrosamine-free accelerator for EPDM and other diene elastomers, used as a Secondary accelerator in the efficient vulcanization of NR and other rubbers, such as IR, SBR, NBR, and IIR, EPDM. It is used in conjunction with sulfenamide, thiazole, thiuram and carbamate. It offers very good processing safety and does not bloom, for NR demonstrates excellent reversion and heat aging resistance.
Packing Size: 25 kgs
Available Form: Powder
Technical Data Sheet
Product Name : JC CURE ZBP
Chemical Name : Zinc Dialkyldithiophosphate
Composition : 70 % zinc dialkyldithiophosphate and 30% silica
Appearance : White Powder
Storage : Store in a cool dry place away from moisture and sunlight
Stability : 24 Months from date of manufacture
Advantages
Due to excellent dispersion and solubility a constantly high quality is achieved. Cycle times can be shortened by high crosslinking rates. Faster extrusion speeds are also achievable. Lifetimes increased due to resistance to thermal ageing. Freedom from nitrosamines and poisonous substances, solve occupational health problems.
Effective as a desiccant in both plastic as well as rubber applications. Packing Size: Customized as per requirement. Available Forms: Powder Technical Data Sheet Product Name : JC CaO - T Chemical Name : Calcium Oxide (treated with1% Organic Compound) Appearance : Fine white/off whitepowder. Solubility : Insoluble in water and soluble in mineral acids Special features : JC CaO T is made from soft stone with advance calcination technology which is resulting with high surface area, high activity and low Iron content. Special surface coating enhances the dispersion in rubber and plastic applications. There will be not any unintended reaction with humidity. Mode of action : Calcium Oxide binds the moisture by the formation of calcium hydroxide, hence used as a desiccant to remove excessive moisture from rubber compounds CaO is preferably used in extrusion compounds which have to be cured continuously either in open air, like (fluid beds, salt baths) or in UHF curing process like (microwave units, and hot air channels), also used in the foamed compounds to improve the cell structure and surface finish of the end product. It can be effectively used in reprocessing of thermoplastic materials. Calcium Oxide : 94% Min. So. Gr. at 25oC : 3.3 + 0.1 Bulk Density (gm/ml) : 0.65 + 0.1 Al2O3 : < 1.0 % SiO2 : < 2.0 % Fe2O3 : < 0.025 % Sieve residue 325 mesh : < 1.0 % Sieve residue 200 mesh : Nil Mean Parcle Size Micron (D50%) : 4.5 - 6.5 Packing : Customize packing with EVA/PP Bag.(Normally 1 Kg Pack X20 Kg or 10 KgX2 Pack /Bag) Storage : Stored in cool and dry place, moisture strictly avoided Advantages CaOT is preferably used in extrusion compounds which have to be cured continuously either in open air, like (fluid beds, salt baths) or in UHF curing process like (micro wave units, and hot air channels), also used in the foamed compounds to improve the cell structure and surface finish of the end product. It can be effectively used in reprocessing of thermoplastic materials