Characteristics of sintered calcium aluminate: 1) Uniform chemical composition, low melting point and fast melting speed can shorten the refining time; 2) No fluorine, no erosion of furnace lining and ladle; 3) Compact structure, no water absorption, easy storage and transportation; 4) Due to the stable phase and fast slag formation, it can reduce the dust pollution to the iron and steel plant and comprehensively stabilize the refining process; 5) It does not contain impurities such as hydrogen, nitrogen and carbon, which is conducive to improving the quality of steel. Sintered calcium aluminate (premelted aluminum calcium slag) is mainly used in LF furnace, open hearth furnace and converter ladle refining to remove impurities such as sulfur and oxygen in molten steel and reduce the content of harmful elements and impurities in steel. It is suitable for ordinary carbon steel, high carbon steel, high and low alloy steel.
Sintered Calcium Aluminate Sintered Calcium Aluminate ( Sintered Refining Slag) is calcined in the rotary kiln with the high quality raw materials.It�¢??s a good quality refining agent.It is characterized by very strong desulfurization and deoxygenation, low melting point,high melting speed, it can shorten smelting time, reduce the energy consumption,reduce dust pollution in the steel plant,reduce the consumption of the ladle refractory materials,increase the service life of the ladle.
Sintered Calcium Aluminate ( Sintered Refining Slag) is calcined in the rotary kiln with the high quality raw materials.It is a good quality refining agent.It is characterized by very strong desulfurization and deoxygenation, low melting point,high melting speed, it can shorten smelting time, reduce the energy consumption,reduce dust pollution in the steel plant,reduce the consumption of the ladle refractory materials,increase the service life of the ladle. For more information, check
Sintered Calcium Aluminate ( Sintered Refining Slag) is calcined in the rotary kiln with the high quality raw materials.It is a good quality refining agent.It is characterized by very strong desulfurization and deoxygenation, low melting point,high melting speed, it can shorten smelting time, reduce the energy consumption,reduce dust pollution in the steel plant,reduce the consumption of the ladle refractory materials,increase the service life of the ladle.
Sintered Calcium Aluminate ( Sintered Refining Slag) is calcined in the rotary kiln with the high quality raw materials. It s a good quality refining agent.It is characterized by very strong desulfurization and deoxygenation, low melting point,high melting speed, it can shorten smelting time, reduce the energy consumption,reduce dust pollution in the steel plant,reduce the consumption of the ladle refractory materials,increase the service life of the ladle.
sintered Calcium Aluminate ( Sintered Refining Slag) is calcined in the rotary kiln with the high quality raw materials.It is a good quality refining agent.It is characterized by very strong desulfurization and deoxygenation, low melting point,high melting speed, it can shorten smelting time, reduce the energy consumption,reduce dust pollution in the steel plant,reduce the consumption of the ladle refractory materials,increase the service life of the ladle. For more information
Sintered Calcium Aluminate ( Sintered Refining Slag) is calcined in the rotary kiln with the high quality raw materials.It is a good quality refining agent.It is characterized by very strong desulfurization and deoxygenation, low melting point,high melting speed, it can shorten smelting time, reduce the energy consumption,reduce dust pollution in the steel plant,reduce the consumption of the ladle refractory materials,increase the service life of the ladle.
We are proposing about 2000tons of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag - European Code: 19.12.01 - Basel Code: B1010 - HS Code: 2619.0020 - Quantity: 2000 tons currently available - Monthly quantity: 500-1000 tons depending on production - Size: 350 1200 mm - Fe content: from 77 to 86% - C content: above 2,5-3% - Bulk density: 2,8-3,4 tons/m3 - Loading type: loose in 20 (26-27 tons on average) The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact us
This Cast Iron slag is a by-product derived from the production of thermal insulating products. The byproduct is a ferrous slag which can be utilised in an electric arc furnace to produce crude steel. Physical Description On visual inspection, it appears to be made up of irregular shapes. Dimension: 500mm -800mm Chemical Composition Its chemical composition is homogeneous and stable with Fe contents in the range of 90 +/- 5% and P contents < 0.6% S around 0.15% and C% around 3.5%. Packing: Loose in container Loading: in 20 Container For further information, please feel free to contact us.
We are proposing about 1000 1200 Mt/ton monthly of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag : 1. >85% Fe Average 600mm Max Fraction 2. >78% Fe Average 20-300mm Fraction The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact