The A Grade of Tire Compounds are supplied from the tire factories which are mainly in USA, Europe and the Far East. The compound`s content is Natural Rubber and Syntehtic Rubber ((S)SBR, BR).
The materials have original tire compound`s chemical additives because of that vulcanization time is long so its shelf life is long. Users who use these goods must add some accelerators while mixing them. The goods have high elasticity, high abrasion resistance, low degree of deformation because of that the goods are preferred by users
A GRADE COMPOUND
Goods A Grade Tire Compound
Type Wigwag
Vulcanization %0
Tensile Strength Min. 14 MPa
Hardness 60 Shore A (+/- 5)
Abrasion 100 - 130
Elongation 400 - 650
Density 1.15 g/cm3 (+/- 0.05)
Quantity 20' 16 MT, 40' 24 MT
Features
Wet Hold Resistance
Wear Resistance
Excellent Flexibility
Low Heat Resistance
Impact Durability
Easy Processing
Good Adhesion
Weather Resistance
B GRADE COMPOUND
Goods B Grade Tire Compound
Type Wigwag and Tread
Vulcanization Up to % 10
Tensile Strength Min. 15 MPa
Hardness 60 Shore A (+/- 5)
Abrasion 100 - 130
Elongation 400 - 650
Density 1.15 g/cm3 (+/- 0.05)
Quantity 20' 15 MT, 40' 23 MT
Features
Wear Resistance
Excellent Flexibility
Impact Durability
Heat Aging Properties
Easy Processing
Good Adhesion
C GRADE COMPOUND
Goods A Grade Tire Compound
Type Wigwag and Tread
Vulcanization Up to % 15
Tensile Strength Min. 14 MPa
Hardness 60 Shore A (+/- 5)
Abrasion 100 - 130
Elongation 400 - 650
Density 1.15 g/cm3 (+/- 0.05)
Quantity 20' 15 MT, 40' 23 MT
Features
Wear Resistance
Excellent Flexibility
Impact Durability
Good Adhesion