Characteristics
1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed.
2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products.
3.High mechanical strength and strong deoxygenation and desulfuration effects.
Model Chemical Composition% Si Mg Ca Re Ba La Fe BN-126 38-44 6-7.5 1.0-3.0 1.8-2.5 - balance BN-127 38-44 6.3-7.5 2.0-3.5 2.5-4.0 1.2-2.0 balance BN-137 38-44 6.3-7.5 1.0-3.0 2.5-4.0 - balance BN-138 38-44 7.0-9.0 2.0-3.0 2.0-4.0 - balance BN-158 38-44 7.0-9.0 2.0-3.0 4.0-6.0 - balance BN-101 44-48 5.6-6.5 0.8-1.2 - ï¼?2.0 proper balance BN-104 44-48 5.5-6.5 1.0-1.5 0.4-0.6 proper balance Standard Size: 0.6-6mm,1-12mm,5-25mm,4-30mm Packing: 25kg woven plastic bag in 1mt jumbo bag. Note: Chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements. Characteristics 1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed. 2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products. 3.High mechanical strength and strong deoxygenation and desulfuration effects.
Model Chemical Composition% Si Mg Ca Re Ba La Fe BN-126 38-44 6-7.5 1.0-3.0 1.8-2.5 - balance BN-127 38-44 6.3-7.5 2.0-3.5 2.5-4.0 1.2-2.0 balance BN-137 38-44 6.3-7.5 1.0-3.0 2.5-4.0 - balance BN-138 38-44 7.0-9.0 2.0-3.0 2.0-4.0 - balance BN-158 38-44 7.0-9.0 2.0-3.0 4.0-6.0 - balance BN-101 44-48 5.6-6.5 0.8-1.2 - ï¼?2.0 proper balance BN-104 44-48 5.5-6.5 1.0-1.5 0.4-0.6 proper balance Standard Size: 0.6-6mm,1-12mm,5-25mm,4-30mm Packing: 25kg woven plastic bag in 1mt jumbo bag. Note: Chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements. Characteristics 1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed. 2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products. 3.High mechanical strength and strong deoxygenation and desulfuration effects.