Zirconia fused aluminum oxide
Chemical Composition(%)
ItemsAl2O3ZrO2 TiO2 Fe2O3SiO2
ZA2568-7224-301.5 0.5 1.0
ZA4055-5735-441.5 0.5 1.0
Physical Properties
Crystal Form:Monoclinic tetragonal system
Reaction with acid and alkali:no
Reaction with carbon:Forming carbide since 1650C
Color:Grey
True Density:4.20g/cm3
Bulk Density:2.18g/cm3
Moh's hardness:9.0
Knoop hardness:1450-2000kg/cm2
Melting point:1900C
Maximum service temperature:1700C
Specific heat capacity(cal/g.C):0.2205(50-500C)
Heat conductivity:0.2718 cal/cm2.sec.C
Linear expansivity(X10-6);6.82(100-700C)
Main Applications
1.Making zircon fused alumina brick and building materials
2.Used for making bonded abrasives products,and process of grinding,sandblasting,surface treatment of metal products and other materials.
3.With good melt erosion resistance,Zirconia fused alumina has good grinding effect on steel,iron casting,heat resistant steel and other alloy materials.
4.Zirconia fused alumina can be made for heavy duty Zirconia fused alumina grinding wheel,snagging,cutting disc,Fiber disc,grinding rails,high speed abrasive belts etc
5.Used for making coated abrasives products,
6.Used for making lapping paste,polishing wax,emery cloth,sandpaper etc
Available Sizes
0-0.5mm 0.5-1mm 1-1.5mm 1-2mm 1-3mm 100F 200F 325F
F4 F5 F6 F7 F8 F10 F12 F14 F16 F20 F22 F24 F30 F36 F46 F54 F60 F70 F80 F90 F100 F120 F150 F180 F220#4#5#6#7#8#10#12#14#16#20#24#30#36#46#54#60#70#80#90#100#120#150#180#220
Aluminum oxide Alumina powder for Electric vacuum tube shell ceramic Al2O3 item value Classification ALUMINA CAS No. 1344-28-1 Other Names Alumina MF Al2O3 EINECS No. 215-691-6 Grade Standard Electron Grade, Industrial Grade, Reagent Grade Purity 99.5% Appearance White powder Application electronic ceramics Color White Grade Industrail Grade Density 3.5 g/cm3 Melting point 2054 Boiling Point 2980 Molecular Weight 101.96 Shape Ionische Water Solubility Hard Packing 25 Kg Pp Bag or plastic barrel Sample Availiable
Aluminum Oxide(CAS:11092-32-3)
Zinc >55%
Supplier: Iron oxide, zinc product, aluminum, rutile, ilmenite, struverite, monazite, etc
Buyer: Metal ores, zircon sand
CAS 1344-28-1 EINECS 215-691-6 Chemical Formula Al2O3 Appearance White amorphous powder Molecular weight 101.961 Melting point 2050
Zirconia fused alumina Brief introduction Zirconia fused alumina was made from aluminum and Zirconium oxide by melting above 2000 in the electric arc furnace and cooling.Then the huge Zirconiafused alumina lump be crushed into different size,from a few mm to 0.8 um. Zirconia fused alumina physical properties chemical composition(%) GradeZrO2Al2O3TiO2Fe2O3SiO2 ZA2524%-30%68%-72%5%max0.5%max1.0%max ZA4035%-44%55%-57%1.5%max0.5%max1.0%max physical properties 1ColorGray 2True density4.20g/cm3 3Bulk density2.18g/cm3 4Moh's hardness9.0 Zirconia fused alumina size &Application 1.Application :top refractory, slide gate nozzle,submersed nozzle,brick ,building materials. Section sand0-1mm,1-3mm, 3-5mm,5-8mm,etc Fine powder100f,200f,325f ,etc. 2.Application :bonded abrasives,abrasives belt,grinding,heavy duty wheel grinding, cutting discï¼?fiber discïrinding rails Granularity sand/granular sand / grit size sand/grain size sand FEPAF4F5F6F7F8F10F12F14F16F20F22F24F30F36F40F46F54F60F70F80F90F100F120F150F180F220 JIS4#5#6#7#8#10#12#14#16#20#22#24#30#36#40#46#54#60#70#80#90#100#120#150#180#220
Alumina (Aluminium Oxide) is the most widely used oxide ceramic material. Its applications are widespread, and include spark plugs, tap washers, abrasion resistant tiles, and cutting tools. Very large tonnages are also used in the manufacture of monolithic and brick refractories.
Pink Fused Alumina, also called Pink Fused Aluminium Oxide, Chromium Aluminum Oxide, abbreviated as "PA", belongs to the group of artificial corundum. It's made from fusion of high purity alumina powder and chromium oxide in electric arc furnace. Because of its chrome content, it's a pink color material. Its main content is Aluminium Oxide(Al2O3), with little content(about 0.7% Chromium Oxide and about 0.3% Sodium Oxide(Na2O). Pink Fused Aluminium Oxide is a hard, tough, self-sharpening, low magnetic, coarse grits, pure and clean abrasive material. Compared to White Fused Aluminium Oxide, it has similar hardness, while better strength and cutting side. It's widely used in production of vitrified grinding wheel, resinoid grinding wheel, cutting discs, grinding head and other abrasive tools, also for sandblasting abrasvies, polishing, free grinding, cutting etc.
Tabular Alumina Al2O3 99.2% min Tabular Alumina: The plate-like crystal structure has small pores and many closed pores, and the porosity is roughly the same as that of fused corundum. It has high purity, good volume stability and minimal reheating shrinkage. The refractory or castable used for production has good thermal shock stability and bending strength after high-temperature treatment, but the price is higher than that of other alumina. High fire resistance; High corrosion resistance; High erosion resistance; High thermal shock stability; High strength and good toughness; Stable chemical properties. Tabular corundum is a kind of pure sintered corundum with complete shrinkage without adding any additives such as It has the characteristics of coarse crystal and good development crystal structure. The plate-like crystal structure has small pores and many closed pores, and the porosity is roughly the same as that of fused corundum. It has high purity, good volume stability and minimal reheating shrinkage.