Non-halogen intumescent flame retardant
Appearance
White powder
Phosphorus mass fraction%
22.0-24.0
Water content %
0.5max
Density g/cm3
About 1.8
Bulk density g/cm3
About0.4
Thermal decomposition onset, scan rate 30f¦/min, f¦
250 min
Particle size , um
About 25
Key properties:
Gd-app104 is a non-halogenated flame retardant based on gd-app101, which develops its effectiveness through phosphorus/nitrogen synergism. When incorporated into polyolefine, it shows high processing stability and no migration.
Gd-app104 differs in its mode of action from halogenated flame retardants in the fire. When the polyolefine on exposure to flame, the carbon foam layer formed protects the polymer through its heat insulating effect to reduce further oxygen access and prevent dripping of the polymer. At the same time there are no thrill halogen hydride gases to produce.
Applications:
Gd-app104, may be mostly used in a range of thermoplastics, especially pp, pe, eva, tpe and rubber etc., which is suitable extrusion and injection moulding applications. Of course it may be suitable for use in hot melt adhesives or coating compounds.
Fiber drum, kraft bag, woven pvc bag(polyethylene liner)
Ammonium polyphosphate
Appearance
White powder
Whiteness (reflectance), %
92.0 min
Ph, 10% slurry, 25¦
6.0-7.5
Acid value, mgkoh/1gapp
1.0max
Solubility in water , 25¦, g/100mlh2o
0.50 max
Total nitrogen, %
14.0-15.0
Phosphorus (as p2o5), %
72.0-74.0
True density, g/cm3
About 1.9
Bulk density, g/cm3
0.6-0.7
Viscosity, 10% slurry, 25¦, mpa.S
80 max
Degree of polymerization
1000 min
Thermal decomposition onset, scan rate 30¦/min, ¦
285 min
Average particle size, 50%pass, um
5-25
Particle size, 98%pass, um
10-43
Key properties:
1, low water solubility gd-app101 has low water solubility which makes it useful in application where the product is exposed to high humidity conditions or water.
2, high phosphorus content -gd-app101 contains 72.5% phosphorus (as p2o5) which makes it a very effective fire retardant.
3, nearly neutral ph-gd-app101 can be neutralized or brought to the alkaline side by the addition of small amounts od ammonium hydroxide.
4, non-halogen-gd-app101 is a highly effective non-halogen fire retardant.
Applications:
Gd-app101 is an effective fire retardant for applications such as:
1, intumescent latex and solvent based paints.
2, intumescent mastic, caulks and putties.
3, polymer systems such as polyethylene, polypropylene, polyurethane,
4, rubbers, acrylics, polyterephthalate.
5, building materials such as wall coverings, ceiling tiles, roofing products, wall panels, wood chip board.
Fiber drum, kraft bag, woven pvc bag(polyethylene liner)
Melamine cladding ammonium polyphosphate
Appearance
White powder
Whiteness (reflectance), %
92 min
Ph, 10% slurry, 25¦
7.5-9.0
Solubility , 25¦, g/100mlh2o
0.15 max
Total nitrogen, %
18.0 min
Phosphorus (as p2o5), %
68.0 min
True density, g/cm3
About 1.9
Viscosity, 10% slurry, 25¦, mpa.S
20 max
Degree of polymerization
1000 min
Thermal decomposition onset, scan rate 30¦/min, ¦
290 min
Average particle size, 50%pass, um
10-25
Particle size, 98%pass, um
15-43
Key properties:
Gd-app102 melamine cladding ammonium polyphosphate is gd-app101ammonium polyphosphate modified by melamine on the surface.
1, very low water solubility -gd-app102 has low water solubility that is no more than 0.10g/100mlh2o at 20¦, which makes it useful in application where the product is exposed to high humidity conditions or water.
2, high phosphorus content and nitrogen content-gd-app102 contains 68.0% phosphorus (as p2o5) and 18.0%nitrogen which makes it a very effective fire retardant.
3, low viscosity +c viscosity of gd-app102 is below 20mpa.S.
4, thermal decomposition onset that is above 295¦, which makes it be widely used to plastic with different melt-point temperature.
5, non-halogen-gd-app102 is a highly effective non-halogen fire retardant.
Applications:
Gd-app102 is an effective fire retardant for applications such as:
1, intumescent latex and solvent based paints.
2, polymer systems such as polyethylene, polypropylene, polyurethane, rubbers, acrylics, polyterephthalate.
3, building materials such as wall coverings, ceiling tiles, roofing products, 4, wall panels, wood chip board.
Fiber drum, kraft bag, woven pvc bag(polyethylene liner)
Epoxy resin cladding ammonium polyphosphate
Appearance
White powder
Whiteness (reflectance), %
94 min
Ph, 10% slurry, 25¦
5.5-7.5
Solubility , 25¦, g/100mlh2o
0.1 max
Total nitrogen, %
18.0 min
Phosphorus (as p2o5), %
68.0 min
True density, g/cm3
About 1.9
Viscosity, 10% slurry, 25¦, mpa.S
20 max
Degree of polymerization
1000 min
Thermal decomposition onset, scan rate 30¦/min, ¦
290 min
Average particle size, 50%pass, um
10-25
Particle size, 98%pass, um
20-43
Key properties:
Gd-app103epoxy resin cladding ammonium polyphosphate is gd-app101
Ammonium polyphosphate modified by epoxy resin on the surface.
Characteristic of gd-app103:
1, reduce water solubility;
2, reduce air hygroscopicity;
3, reduce viscosity in water;
4, obviously improve dispersibility and compatibility with plastic materials;
5, increase fluidity of powder;
6, improve thermal expansion efficiency during inflaming retarding process.
Applications:
Gd-app103 is an effective fire retardant for applications such as:
1, various kinds of expanding fire-refractory coating;
2, thermal plasticity polyolefin and unsaturated arene plastic;
3, isocyanurate foam;
4, epoxy resin and unsaturated resin;
5, cable and rubber;
6, plastic material of electron device.