Key characteristics of this Kazakhstan-sourced cotton include:
Average micronaire value of 5.06, indicating medium to fine fiber fineness
Mean staple length of 1.135 inches (28.83 mm)
Average fiber strength of 30.8 g/tex
Mean uniformity index of 83.0%, suggesting good fiber length consistency
Average color grade between 42-2 and 52-1, indicating a light color
This cotton demonstrates consistent quality across multiple parameters, making it suitable for various textile applications requiring medium to fine fibers with good strength and uniformity.
Key Features:
High-quality cotton fiber sourced from Kazakhstan's fertile fields
Exceptional strength and durability (Strength: 30.9 g/tex)
Superior length (Upper Half Mean Length: 1.194 inches / 30.33 mm)
Excellent uniformity (Uniformity Index: 84.7%)
Bright white color (Reflectance Rd: 77.4)
Low trash content (Trash Count: 13)
Average Micronaire: 4.32, indicating ideal fiber fineness and maturity
Average Length: 1.134 inches (28.8 mm), perfect for spinning into smooth, strong yarns
Average Strength: 31.1 g/tex, ensuring durability in finished products
Average Uniformity: 83.1%, promising consistent quality in fabric production
Our cotton undergoes rigorous testing using industry-standard CSITC and ITMF protocols, guaranteeing reliability and consistency. With its balanced characteristics, this Kazakh upland cotton is ideal for producing high-quality fabrics, from comfortable apparel to durable home textiles.
Technical Specifications:
Fiber Length: 17-20 mm
Material: 100% Cotton Comber Noil
Moisture Content: 6.0-6.5%
Color: Natural
Quality: Premium Grade Comber Noil
Purity: High
Product Features:
High-quality short fibers extracted during combing process
Clean and contamination-free
Homogeneous fiber distribution
Good strength properties
Uniform fiber structure
This Ne-20/1 carded ring yarn, originating from Turkmenistan, is a premium textile product designed for high-performance applications. With an average linear density of 19.82 Ne, this yarn offers an optimal balance of fineness and strength.
The yarn boasts exceptional uniformity, demonstrated by its low U% of 10.47 and CVm% of 13.35. These characteristics ensure consistent texture and appearance in the final fabric. Its minimal thin and thick places contribute to an even surface, while the controlled nep count enhances the overall quality.
Strength is a key feature of this yarn, making it suitable for demanding textile processes. The yarn's durability is complemented by its well-balanced structure, featuring an average hairiness index of 16.35. This controlled hairiness contributes to a soft hand feel while maintaining fabric integrity.
With an impressive tenacity averaging 72.41 cN/tex, this yarn is capable of withstanding high tension during both manufacturing and end-use. Its versatile properties make it ideal for a wide range of applications in both woven and knitted fabrics.
This Ne-20/1 carded ring yarn is perfect for producing high-quality textiles that require a combination of strength, uniformity, and refined texture. It's particularly suitable for apparel, home textiles, and technical fabric applications where performance and aesthetics are equally important.
Yarn Count: 30/1 Ne (English Cotton Count)
Yarn Type: Compact Ring-Spun
Fiber Composition: 100% Cotton
Processing: Combed
Twist: 650 T/m (Turns per meter), Z direction
Application: Knitting
Origin: Uzbekistan
Key Quality Parameters:
Average U%: 9.21%
Average CVm%: 11.63%
Average Thin Places (-50%): 0 per km
Average Thick Places (+50%): 16 per km
Average Neps (+200%): 19 per km
Total IPI (Standard): 35 per km
Test Method Explanation:
The test was conducted using the USTER�® TESTER 6, which is an industry-standard instrument for yarn quality testing. Here are the key aspects of the testing method:
Equipment: USTER�® TESTER 6 (version 21.7.5.0)
Test Speed: 400 m/min
Test Duration: 1 minute per test
Test Length: 400 meters per test
Number of Tests: 5 tests performed
Testing Conditions:
Temperature: 25.0�°C
Relative Humidity: 48.0%
Measuring Slot: Automatic MS4
Analysis Type: Short IP (Imperfection) analysis
USTER�® STATISTICS used: 2018 edition for 100% Cotton, ring yarn, combed, package, knitting
Key Features:
Composition: 100% Cotton
Count: 30/1 Ne
Twist: 1,000 T/m
Production Method: Open End (OE) Rotor spinning
Processing: Carded
Application: Weaving
Technical Specifications:
Unevenness (U%): 11.89%
CVm: 15.03%
CVm (1m): 2.85%
CVm (10m): 1.54%
Thin Places (-50%): 53 /km
Thick Places (+50%): 97 /km
Neps (+200%): 844 /km
Total IPI (Standard): 219 /km
Hairiness (H): 3.84
Testing Standards:
This yarn quality report was generated using the USTER�® TESTER 6 (version 21.7.5.0) and follows the USTER�® STATISTICS 2018 for 100% CO, rotor yarn, carded, package, weaving.
Test Conditions:
Test speed: 400.00 m/min
Test time: 1.00 min
Test length: 400.00 m
Temperature: 25.2 �°C
Relative humidity: 48.2 %
Key Specifications:
Count: 30/1 Ne
Spinning Method: OE Rotor
Fiber: 100% Cotton (4.50 Micronaire, 29.00 mm staple length)
Twist: 650 T/m, Z direction
Processing: Carded
Primary Application: Knitting
Technical Details (USTER TESTER 6 Results):
Unevenness (U%): 11.39
Coefficient of Mass Variation (CVm%): 14.36
CVm (1m): 4.23%
CVm (10m): 2.94%
Thin Places (-50%): 19 /km
Thick Places (+50%): 62 /km
Neps (+200%): 420 /km
Hairiness (H): 4.11
Key features include:
Material: 100% Cotton (4.50 Mic)
Count: 32.00 Ne
Twist: 820.00 T/m, Z direction
Processing: Carded
Application: Knitting
Yarn type: Compact
Physical properties (USTER TESTER 6):
Test speed: 400.00 m/min
Test length: 400.00 m
Mean CVm: 13.94%
Mean Thin places (-50%): 0 /km
Mean Thick places (+50%): 130 /km
Mean Neps (+200%): 137 /km
Mean Hairiness (H): 5.21
Mechanical properties (USTER UTR 5):
Test speed: 5000 mm/min
Test length: 500 mm
Mean Breaking Force: 311.01 cN
Mean Elongation: 5.66%
Mean Tenacity: 17.19 RKm
Mean Breaking Work: 451.01 cN.cm
We are proud to offer an extensive range of high-quality yarns to meet various textile manufacturing needs. Our product line includes:
100% Cotton Open-End Yarns:
Available counts: 6/1, 7/1, 8/1, 10/1, 12/1, 16/1, 20/1, 24/1, and 30/1
Ideal for a wide range of textile applications
Superior quality and consistency
Blended Open-End Yarns:
Composition: Cotton waste and cotton blend
Available counts: 6/1, 7/1, 8/1, 10/1, 12/1, 14/1, 16/1, and 20/1
Cost-effective option without compromising on quality
100% Cotton Carded and Compact Yarns:
Available counts: 12/1, 16/1, 20/1, 21/1, 24/1, 30/1, 32/1, 36/1, 38/1, and 40/1
Superior strength and smoothness
Perfect for high-end textile products
Specifications
Count 61 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 116354 gf
Elongation 696
Tenacity 1182 RKm
Breaking Work 223633 gfcm
CV Breaking Force 648
USTER TESTER 4 Evenness Test
U 953
CVm 1199
Thin Places 50 02 km
Thick Places 50 30 km
Neps 200 66 km
Hairiness H 502
Test Methods
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Specifications
Count 101 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 72340 gf
Elongation 645
Tenacity 1225 RKm
Breaking Work 129332 gfcm
CV Breaking Force 745
USTER TESTER 4 Evenness Test
U 935
CVm 1178
Thin Places 50 00 km
Thick Places 50 22 km
Neps 200 58 km
Hairiness H 501
Test Methods
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Specifications
Count 101 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 72340 gf
Elongation 645
Tenacity 1225 RKm
Breaking Work 129332 gfcm
CV Breaking Force 745
USTER TESTER 4 Evenness Test
U 935
CVm 1178
Thin Places 50 00 km
Thick Places 50 22 km
Neps 200 58 km
Hairiness H 501
Test Methods
Specifications
Count 141 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 46326 gf
Elongation 441
Tenacity 1177 RKm
Breaking Work 60081 gfcm
CV Breaking Force 870
USTER TESTER 4 Evenness Test
U 1030
CVm 1300
Thin Places 50 10 km
Thick Places 50 146 km
Neps 200 618 km
Hairiness H 445
Test Methods
Specifications
Count 141 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 46326 gf
Elongation 441
Tenacity 1177 RKm
Breaking Work 60081 gfcm
CV Breaking Force 870
USTER TESTER 4 Evenness Test
U 1030
CVm 1300
Thin Places 50 10 km
Thick Places 50 146 km
Neps 200 618 km
Hairiness H 445
Test Methods
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Specifications
Count 71 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 102413 gf
Elongation 549
Tenacity 1214 RKm
Breaking Work 164380 gfcm
CV Breaking Force 701
USTER TESTER 4 Evenness Test
U 939
CVm 1182
Thin Places 50 00 km
Thick Places 50 10 km
Neps 200 194 km
Hairiness H 645
Test Methods
Strength USTER UTR 5 5000 mmSpecifications
Count 101 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 72340 gf
Elongation 645
Tenacity 1225 RKm
Breaking Work 129332 gfcm
CV Breaking Force 745
USTER TESTER 4 Evenness Test
U 935
CVm 1178
Thin Places 50 00 km
Thick Places 50 22 km
Neps 200 58 km
Hairiness H 501
Test Methods
Specifications
Count 141 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 46326 gf
Elongation 441
Tenacity 1177 RKm
Breaking Work 60081 gfcm
CV Breaking Force 870
USTER TESTER 4 Evenness Test
U 1030
CVm 1300
Thin Places 50 10 km
Thick Places 50 146 km
Neps 200 618 km
Hairiness H 445
Test Methods
Specifications
Count 141 Ne
Composition 100 Cotton
Spinning Method OpenEnd OE Rotor
Application Weaving
Test Results
USTER UTR 5 Strength Test
Breaking Force 46326 gf
Elongation 441
Tenacity 1177 RKm
Breaking Work 60081 gfcm
CV Breaking Force 870
USTER TESTER 4 Evenness Test
U 1030
CVm 1300
Thin Places 50 10 km
Thick Places 50 146 km
Neps 200 618 km
Hairiness H 445
Test Methods
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Strength USTER UTR 5 5000 mmmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min durationmin 500 mm test length
Evenness USTER TESTER 4 400 mmin 25 min duration
Specifications:
Count: 8/1 Ne
Composition: 100% Cotton
Spinning Method: Open-End (OE) Rotor
Application: Weaving
Test Results:
USTER�® UTR 5 (Strength Test):
Breaking Force: 812.72 gf
Elongation: 6.84%
Tenacity: 11.01 RKm
Breaking Work: 1,505.56 gf.cm
CV (Breaking Force): 9.93%
USTER�® TESTER 4 (Evenness Test):
U%: 11.00%
CVm: 13.93%
Thin Places (-50%): 2.8 /km
Thick Places (+50%): 17.0 /km
Neps (+200%): 57.2 /km
Hairiness (H): 6.32
Test Methods:
Strength: USTER�® UTR 5 (5000 mm/min, 500 mm test length)
Evenness: USTER�® TESTER 4 (400 m/min, 2.5 min duration)