By coating a layer of metal powder on the ceramic surface and sintering at high temperature to form a solidified and dense metallized layer, so as to realize the welding of ceramic and metal.
Technical parameters
Density (before sintering) 3.15±0.1g/cm
Density (after sintering) 6.05±0.03g/cm
Three point bending strength 1200Mpa
The chemical solubility after sintering is
Characteristic
Product Name G050060025
Specification: Length: 50.0±1.0mm
Outer Diameter: 6.0±0.1mm
Inner Diameter: 2.5±0.1mm
Appearance: no stain and crack; no impurities; no oxidation.
Voltage: can be customized according to customers needs
Electrode: Electrodes are welded with nickel wire can be customized according to customers needs
Lead tension: horizontal pull 5KGf Vertical tension 3KGf
High-voltage insulation test: 3700V/1S leakage current 0.62mA
Insulation resistance: >100M 500VDC Characteristic
Characteristic
1. High temperature resistance, corrosion resistance, no infiltration with nonferrous metal melt such as aluminum melt.
2. Excellent thermal conductivity, strong thermal shock resistance and no cracking.
3. Oxidation resistance and long service life.
4. It can be customized according to customer requirements and specifications.
Solid PCBN inserts series
Widely applied in finishing, semi-finishing and roughing.
High fracture toughness, suitable for continuous cutting, general cutting, and interrupted cutting.
More cutting edges, higher utilization rate.
Higher bending strength, suitable for large cutting depth (