TWO COMPONENT ACRYLIC BASED MATTE VARNISH
PRODUCT DESCRIPTION
Product type ACRYLIC
Gloss 20-25 gloss �± 5
Solid Matter by Volume (%) 55 �± 1
Solid Matter by Weight (%) 56 �± 1
Theoretical Coverage (m�² / kg)
Recommended application amount (6-7.5 dry film thickness 30-35�µ) 100-120 g for one layer
POT LIFE SA (20 �ºC) 24
Density (g / cm�³) 0.99 + - 0.03
Powder drying, Touch drying, Stacking dry (20 �ºC / minute) 10-15 minutes-30-40 minutes-18-20 hours
Full Curing 24 hours (20�ºC)
Mixing Ratio A.V.W-1020 1.KOMPENANT 100 parts (By Weight)
A.S.W-01032 2.KOMPENANT 20 parts (By Weight)
Application Thinner Universal acrylic polyurethane thinner 70-80 parts
Application Tools Spray gun Airmix Spray, Roller
Color Transparent
Two Component Polyurethane Based Matt Varnish
PRODUCT DESCRIPTION
Product type Polyurethane
Brightness 40-45 gloss ± 5
Volume Solids (%) 57 ± 1
Solid Matter by Weight (%) 60 ± 1
Theoretical Coverage (m / kg) 10-12 dry film thickness 30-35
POT LIFE SA (20 C) 5
Density (g / cm) 0.93 + - 0.03
Powder drying, Touch drying, Stacking dry (20 �ºC / minute) 20-30 minutes-50-70 minutes-24-30 hours
Full Curing 24 hours (20C)
Mixing Ratio P.V.1541-07 1.KOMPENANT 100 parts (By Weight)
P.V.S.07 2.KOMPENANT 25 parts (By Weight)
Application Thinner Universal acrylic polyurethane thinner 35-40 parts
Application Tools Spray gun Airmix Spray, Roller
Color Transparent
TWO COMPONENT POLYURETHANE BASED BRIGHT PAINT
PHYSICAL PROPERTIES
Product type Polyurethane
Gloss 90-95 gloss ± 5
Volume Solids (%) 59 �± 1
Solid Matter by Weight (%) 62 �± 1
Theoretical Coverage (m�² / kg) 7 - 8,5 100-120 gr (30-35 micron dry film)
POT LIFE SA (20ºC) 3
Density (g / cm³) 1.25 + - 0.05
Powder drying, Touch drying, Stacking dry (20 ºC / minute) 20-30 minutes-6-7 hours-72 hours
Full curing and sanding 24 hours (20�ºC)
Mixing Ratio P.B.9021-05- 1.KOMPENANT 100 parts (By Weight)
P.S.S 2.KOMPENANT 50 parts (By Weight)
Application Thinner Universal acrylic polyurethane thinner 20-25 parts
Application Tools Spray gun, Airmix Spray, Roller
Color White