Sio2%- 56.19
Al2O3%- 26.56
Fe2O3%- 4.2
Tio2%- 1.67
CaO%- 0.31
MgO%- 0.52
K2O%- 1.1
Na2O%- 0.38
L-56.13
A-4.85
B-22.06
Whiteness- 23.93
Shrinkage- 13.08
Plasticity- 39.2
Tempreature C- 1184/1190
Cycle min.-50
Dry MOR- 33.1 Kg/Cm2
Fired MOR- 386.2 Kg/Cm2
Sio2%- 48.10
Al2O3%- 36.11
Fe2O3%- 0.45
Tio2%- 0.99
CaO%-0.24
MgO%- 0.32
K2O%- 0.10
Na2O%- 0.19
L-94.20
A-1.21
B-3.32
Whiteness- 88.5
Shrinkage- 4.73
Plasticity- 34.5
Tempreature C - 1209/1220
Cycle min.- 60
SiO2%- 56.19
Al2O3%- 36.98
Fe2O3%- 0.19
TiO2%- 0.58
CaO%- 0.28
MgO%- 0.42
K2O%- 0.08
Na2O%- 0.21
L- 97.12
A- 0.21
B- 2.92
Whiteness- 91.1
Shrinkage - 4.72
Plasticity- 33.9
Tempreature C - 1206/1218
Cycle Min - 60min
Sio2%- 67.7
Al2O3%- 20.9
Fe2O3%- 0.40
Tio2%- 0.45
CaO%- 0.57
MgO%- 0.23
K2O%- 0.08
Na2O%- 0.34
L-90.7
A-0.80
B-7.01
Whiteness- 74.5
Shrinkage- 3.42
Plasticity- 28.6
Tempreature C- 1213/1214
Cycle min.-60
Dry MOR- 14.6 Kg/Cm2
Fired MOR- 102.6 Kg/Cm2
SiO2 - 98.954%
Al2o3 - 0.209%
Fe2o3 - 0.025%
Whitness - 92%
L* - 94.7
a* -0.07
b*- 2.3
Mesh size - 200# , 250#, 300#