Description:
H838E is a cling masterbatch for PE films, which contains polybutylene cling agent from BP Chemical Company.
It is mainly applied to stretching wrap film for pallets, pasture packing film for agriculture, and adhesive film for household.
It is the best cling masterbatch for strengthening the adhesion of PE films.
General:
Apperance: Milk-White
Processing Method: CPE
Additive Content: 50%
Bulk Density: 500-550 kg/m3
Melt Flow Index ( 190ºC , 2.16kg ):
15-20 g/10min
Moisture Content: < 600ppm
Usage:
.The pellets would not cling to each other, so it is suitable for automatic way of adding the material.
When blending H838E with PE to extrude the film, the Polybutylene cling agent will migrate to the film's surface gradually to make the surface of film with adhesion effect.
.The dosage has to be adjusted according to the change of climate temperature. The suggestion ratio is 0.8% to 2% when the temperature is higher than 15ºC, and 2% to 5% for the temperature is lower than 15ºC.
25kg/Bag
Description:
ZT812 is a masterbatch designed for improving the stiffness of film.
Through the nucleation effect created by the hydrogenated petroleum resin in the masterbatch in the crystallization progresses of polypropylene, to improve the ctrystallization of the film and reduce the variance of the molecule, so that to improve the Young's Modulus and the stiffness of the film.
General:
Apperance: Natural
Additive Content: 50%
Bulk Density: 520 - 560 kg/m3
Melt Flow Index( 230ºC , 2.16kg ):
25 - 45 g/10min
Moisture Content: < 800ppm
Usage:
. ZT812 should be used in core layer, and dosage is suggested to 18% to 22%.
It can improve the obstructing performance as well as the heat sealing and heat shrinking ability at the same time.
. Because ZT812 has a good compatibility with polypropylene, and has an appropriate plasticization, the processing temperature can be properly decreased.
Validity Date: 12 months
25kg/Bag
XJH is a professional manufacturer of masterbatch and plastic additives, holding experienced R&D team and workers as well as whole-heartedly service.
Description:
Carrier-free Super Black Masterbatch 988, taking carbon black to 70%, is made of imported high carbon black pigment and pigment additives processed by imported water-cooled masterbatch pelletizing extrusion dedicated mixer.
Technical parameters:
Specific Gravity: 1.85g / m3
Thermal resistance: 200-400 ºC
Melting means: 0.1g / 10min
Moisture: <0.15%
Application:
Applicable to plastic injection molding, pumping tablets and other processes, especially those with a good blue-blackness and phase in PC, PC / ABS alloy, PA series, PS, and is environmentally friendly high black highlighted the high concentration of black masterbatch. This product is qualified through the EU environmental testing and certification company SGS.
Advantages:
1. High black, bright, high-gloss mirror effect can be achieved.
2. Environmentally friendly, non-toxic, tasteless, surface smoothness and stability of solid color glossy color, good toughness, does not appear the color point and color patterns such phenomena, not only reduce costs, save additives, but also reduce the plant site contamination.
Usage:
Well stir with material before production.
Dosage:
Recommended dosage of 1% to 3% (depending on the product features, requirements).
25kg/Bag
XJH provides two models of cling masterbatch, including H838E & H838.
H838:
H838 is a cling masterbatch for PE films, which contains polybutylene cling agent from BP Chemical Company.
It is mainly applied to stretching wrap film for pallets, pasture packing film for agriculture, and adhesive film for household.
It is the best cling masterbatch for strengthening the adhesion of PE films.
General:
Apperance: Milk-White
Additive Content: 40%
Bulk Density: 500-550 kg/m3
Melt Flow Index( 190ºC , 2.16kg ):
8 - 10 g/10min
Moisture Content: < 600ppm
Usage:
.There is adhesion between the pellets, so it is only suitable to add the material by humans. When blending H838 with PE to extrude the film, the Polybutylene cling agent will migrate to the film's surface gradually to make the surface of film with adhesion effect.
.The dosage had to be adjusted according to the change of climate temperature. The suggestion ratio is 3% to 5% when the temperature is higher than 15ºC, and 4% to 8% for the temperature is lower than 15ºC.
25kg/Bag
Description:
XJH¡¯s rubber deodorizer and plastic deodorizer are developed to remove the noxious gas, peculiar smell and odor existed in rubber and plastic materials.
XJH¡¯s deodorizer is a combination of absorbent and active agent.
Advantages:
1. To absorb CO, SO, NOX, NH, pesticide residue and moisture, etc.
2. To react with alkaline off-flavor substances ( such as NH ) or acidic off-flavor substances ( such as hydrogen sulfide ) to produce plastics of deodorizing function.
3. To maintain the physical performance and mechanical strength of rubbers and plastics.
Application:
Auto Accessories, Toys, Tableware, Food Packages, Office Supplies, Plastic Tubes, etc.
Dosage:
Granule Models: 1% - 4%
Powder Models: 0.4% - 0.8%
*** Adding slipping agents or dispersing agents will make higher efficiency.
25kg/Bag