Size: 12.7mm-120mm Surface hardness: hrc58-66 Chemical elements: c: 1.8-3.3; si: 0.3-1.2; mn: 0.3-1.0; s & p: 0.1max; cr: 10-30( details can be adjusted by users demand). Id from 12.7mm to 130mm high chrome grinding media
Cast grinding balls High chrome casting grinding iron ball for mining Application of chrome grinding balls : 1)cement plants 2)mines 3)power stations 4)chemical industries 5)grinding mill, ball mill, coal mill Features of cast balls: 1) in general, high chrome casting grinding iron balls are famous for high hardness: surface hardness is to 60-68 hrc and volume hardness of 58-65 hrc; 2) high impact toughness: impact toughness is more than 12 j/cm2; 3) low broken rate: the actual broken rate is not higher than 1%; 4) wear-resistant: loss of grinding round rate is 80-500g/ton; Specification: 20-150mm Packing term 1) steel drums (with pallet): 850-900kg/drum 2)container bags: 1000kg/bag Steel drum or container bags
1 high chrome casting balls Size: 6mm-120mm Hardness: hrc60-66; chrome content: 10-30% 2 low chrome casting balls Size: 6mm-120mm Hardness: hrc46-53; chrome content: 0.5-3.5% Packing: 1.Container bags 2. Steel drums The major character of our grinding balls is that: high hardness, no breakage, lower wearing, lower price. It is mainly used in cement plants, mines, power stations etc. Our factory manufacture and export high chrome casting ball as follows: Specifications: 1) diameters: dia. 17 - 130mm 2) hardness: hrc 58-63 3) chemical elements(%): C:1.9-3.3 , si:0.3-1.0 , mn:0.2-0.8 , cr:10.0-30.0, p:0. 9 max , s:0.9 max Characteristics: A) high hardness b) no breakage c) even wearing d) good wear resistance Applied fields: A) mines b) cement plants c) power stations d) chemical industry Outer packing: Container bags, steel drums High chrome a Container bags, steel drums
Our factory manufacture and export high chrome casting ball as follows: Specifications: 1) Diameters: Dia.17 - 130mm 2) Hardness: HRC 58-63 3) Chemical elements(%): C: 2.5-3.2, Si: 1.0 MAX, Mn: 0.5-2.0, Cr: 10-14, P: 0.10 MAX, S: 0.06 MAX Characteristics: A) High hardness B) No breakage C) Even wearing D) Good wear resistance Applied fields: A) Mines B) Cement plants C) Power stations D) Chemical industry Outer packing: Container bags, Steel drums Container bags, Steel drums
High Chrome Cast Grinding Balls Cr12-14% Used in cement, mining and power plant industry. Size: 10-125mm Specifications: C: 2.0-3.4% Si: 1.0%max Mn: 1.0%max P: 0.06%max S: 0.06%max Cr: 12-14% HRC Hardness: 60-66 Microstructure: Martensite + Carbide
Introduction: Dry mill casting steel balls for grinding in power plant Size: diameter 17-150mm Description: High hardness, good wear resistance, good toughness, even wearing, no breakage. Product category: Low chromium casting grinding steel ball Hardness: hrc45-55
Part characteristic The surface hardness of ball will be raised further in using the course, and the wear resistance would gather hard, so can raise mill machine production capacity at the same time, and raises cement ratio surface area and reclaim ratio of the extractive mind. Details view three W dot chinagrindingmedia dot com or Skype: kathysong0425 Specification: A: high hardness in+surface hrc 58-65 and core hrc 56-62 B: good wear resistant C: few breakages D: no mal-roundness. Woven bag or steel drum.
Our cast iron grinding balls can be divided into three categories including the high chromium type, medium chromium type and the low chromium type. 1. The quality index of the high chromium type The chromium content of the high chromium type product is greater than or equal to 10.0%. And the carbon content is between 1.80% and 3.20%. It is required by the national standard that the hardness of the high chromium type product must be no less than 58hrc, and that the impact value should be greater than or equal to 3.0j/cm. This type of product must go through the hot quenching and the tempering treatment to come up to the hardness. Currently at home, there are two quenching methods for this type of product including oil quenching and wind quenching. If the tested hardness of this type of product is below 54hrc, then it shows that the quenching treatment is omitted. 2.The quality index of the medium chromium type The medium chromium type cast iron grinding ball is defined as the chromium content ranging from 3.0% to 7.0%, and the carbon content coming between 1.80% and 3.20%. Its impact value should be no less than 2.0j/cm. . The national standard requires the hardness of this type of product should be greater than or equal to 47hrc. For ensuring the quality, the medium chromium type product should be processed with high temperature tempering to eliminate the casting stress. If the surface of the steel ball assumes the dark red color, it proves that the steel ball has been processed with high temperature tempering. If the surface of the steel ball still comes with the metal color, then, we can judge that the steel ball doesn’t go through the high temperature tempering treatment.
(1) Product Superior raw materials, advanced automated equipment, unique heat treatment technique and strict quality control system contribute to better performance for the general hardness of shandong iraeta grinding steel ball. 1) production standard Yb/t091-2005 2) size: 25-150 mm 3) surface hardness Hrc57-67 hrc 4) volume hardness Hrc56-64 5) breakage rate
Name:Grinding Balls Size:10-150mm Surface Hardness:58-66HRC Breakage:�1% Impact:�3.5J/CM² Why choose Chengxi grinding media: ,Quality management system certified ISO 9001:2008. ,Innovative R&D Design ,High end heat treatment technology ,Strict quality managment system ,Short lead time ,Flexiable customer service