Description FeCrBSi is a solid thermal spray wire used for arc spray systems. It produces a partially amorphous, hard, abrasive and corrosion resistant coating, with a service environment up to 1700° F. High chrome like finishes can be obtained by typical grinding and lapping techniques. FeCrBSi is used in a wide variety of high wear applications, anti-skid surfacing applications and corrosive environments. It can Equivalent to Tafa 95MXC, Armacor M. Applications Boiler Tubes & Tube Shields,Yankee Dryer Rolls ,Anti-Skid ,Fan Blades ,Drill Collars. Product Details Chemical composition Grade Chemical composition(%) FeCrBSi Cr Mn Si B Fe 27~29 1.5-2.0 1~2 3~4 Balance Physical Properties Grade Density Melting point FeCrBSi 7.3g/cm3 1530 °C Typical Deposit Characteristics Typical Hardness Bond Strength Deposit Rate Deposit Efficiency Machilityineab HRC 55-60 6000 psi 10 lbs/hr/100A 0.7 Good Sizes & Packaging: Diameter Packaging      Wire Weight 1/16" (1.6mm) MIG (D 300) 15kg((33 lb)/spool Note that special sizes, or packing requirements are available on all requests.
Rolled copper foil has extraordinary strength, bendability, ductility and lustrous surface, plus its excellent mechanical capacity, makes it irreplaceable as a raw material. Base material:c11000 copper, cu > 99.90% Thickness range:0.0004inch~0.006inch (0.01mm-0.15mm) Width range:0.16inch~24inch (4mm-600mm) Temper:hard, quarter hard, half hard, soft Application:transformer, copper flexible connector, ccl, fccl, pcb, geothermal film, construction, decoration etc. Gb Alloy no. Size (mm) (iso) (asmt) (jis) (bis) (din) T2 Cu-etp C11000 C1100 C101 R-cu57 Thickness: 0.01-0.15/max width: 600 Tu2 Cu-of C10200 C1020 Cu-ofc Of-cu Mechanical properties Temper Jis temper Tensile strength rm/n/mm 2 Elongation a50/% Hardness hv M O 220~275 Â?¥ 15 50~70 Y4 1/4h 240~300 Â?¥ 9 65~85 Y H 330~450 - 100~140 T Eh 380~510 - - Note: we can provide products with other properties according to customers` requirements. Physical properties Density: 8.9g/cm3 Electrical conductivity (20â°c): min 90%iacs for annealed to temper Min 80%iacs for rolled to temper Thermal conductivity (20â°c): 390w/(mâ°c) Elastic modulus: 118000n/m Softening temperature: â?¥380â°c Sizes and tolerances (mm) Thickness Thickness tolerances Width Width tolerances 0.01~0.015 ± 0.002 4~250 ± 0.1 >0.018~0.10 ± 0.002 4~600 >0.10~0.15 ± 0.005 4~600 Specifications available (mm) Thickness Width Temper 0.01~0.015 4~250 O, h >0.018~0.10 4~600 O, h >0.10~0.15 4~600 O, 1/4h, 1/2h, h Carried standard(latest) Nations Standard no. Standard name China Gb/t2059--2000 China's national standard Japan Jis h3100 :2000 Copper and copper alloy sheets, plates and strips U.S.A Astm b36/b 36m -01 Standard specification for brass, plate, sheet, strip and rolled bar
The NiFe alloy is suitable for welding all grades of cast iron but particularly for spheroidal graphite (SG), nodular or ductile irons and some alloy cast irons. It provides compatible strength, ductility and toughness, coupled with good machinability. The NiFe consumables can also be used on some of the high alloy austenitic irons (Ni-Resist). The flake graphite grades are welded with a preheat of 300-350°C but the SG grades are best buttered using low heat input, and low temperature techniques to avoid HAZ hot cracking. Note the martensitic Ni-Hard cast irons and white irons are generally considered to be unweldable because they are too crack-sensitive. The NiFe consumables are also suitable for welding transition joints between cast iron and cast steels, and cast iron and mild/low alloy steels. Typical components are machine bases, pump bodies, engine blocks, gears and transmission housings.
Description ERCuAI-A2 is a copper based filler metal containing about 1% iron used for gas-tungsten arc welding and gas-metal arc welding of copper, copper-nickel, brass, bronze, steel, galvanized steels and also cast iron. Most common applications would include marine maintenance and repair, ship propellers, pump housing, rigging jacks, piston heads, bearings and excellent for build-up or overlaying wear/corrosion resistanceapplications. Combinations of Copper or Aluminum Bronze base metals to steel are very common with this filler. Exhibits high mechanical properties and hardness. Applications ERCuAI-A2 is used to weld and join many ferrous and nonferrous metals and combinations of dissimilar metals. Contains an additive to inhibit inter-granular stress corrosion cracking. This is particularly important when welding on C61300 and C61400 base metal. Some applications include building up bearing surfaces, joining and fabricating copper alloys, overlaying for resistance to corrosion and erosion. Product Details Chemical composition: Grade Chemical composition(%) ERCuAI-A2 Cu+Ag Al Fe Si Zn Pb others Bal 8.5~11.0 5.0~1.5 â?¤0.1 â?¤0.02 â?¤0.02 Â
Description Amorphous Alloy is a cored wire specifically designed for arc spray systems. It produces an amorphous, hard, abrasive and corrosion resistant coating, with a service environment up to 1700° F. The inclusion of 2.0% aluminum in the formulation results in extremely high bond strength and particle to particle adhesion. High chrome like finishes can be obtained by typical grinding and lapping techniques. Vecalloy B can be used in a wide variety of high wear applications, anti-skid surfacing applications and corrosive environments. It can equivalent to Vecalloy B. Applications Boiler Tubes & Tube Shields Yankee Dryer Rolls Anti-Skid Fan Blades Drill Collars Hydraulic Shafts Product Details Chemical composition Grade Chemical composition(%) Vecalloy B Cr Nb B Ni Si Mn Al Fe 13 6 4 6 1 1 3 Balance Typical Deposit Characteristics Typical Hardness Bond Strength Deposit Rate Deposit Efficiency Corrosion Resistance HRC 65-70 10000 psi 10 lbs/hr/100A 80% Excellent Sizes & Packaging Diameter Packaging Wire Weight 1/16" (1.6mm) MIG (D 300) 15kg((33 lb)/spool Note that special sizes or packing requirements are available on all requests.
Copper Wire Rod 8 Mm
Electro galvanized wire BWG20 , wire diameter: 0.93-0.95 mm.
The Tire derived Steel or Tire Wire Scrap is a light melting scrap obtained during the shredding and granulation process of used tires. Generally 10% - 20% of the weight of an old passenger car tyre usually consists of steel. An average shredding plant produces about 100-200 MT of steel tyre wire and its quality can vary according to technology, storing and management systems adopted by the producing plants. We can provide tire wire scrap that still contains up to 20% rubber/fiber. This percentage is detected by manual separation test. The material can be loaded loose in 40 HC container. For further details, please feel free to contact us.
We are involved in trading of titanium alloys and all type of titanium contain material like,Rulite, Ilemenite sand, Titanium slag etc