UHP 400mm*1800mm UHP 450mm*1800mm Used in steel, cement and glass manufacturing, expanded graphite - based sealing gaskets, graphite grease, braid, brushes, brake lining, etc.
Artificial graphite electrode is made of high-quality low ash materials, such as petroleum coke, needle coke and coal pitch.after calcining,burdening,kneading,forming,baking and pressure impregnation, graphitization and then precision machined with professional CNC machining.such of the products own characteristics with low resistivity, good electrical conductivity ,low ash, compact structure,good anti oxidation and high mechanical strength, so it is the best conductive material for electric arc furnace and smelting furnace.
UHP HP RP graphite electrode Φ400-700mm,length 1800mm 2100mm 2400mm 2700mm
The graphite electrode is mainly made of petroleum coke and needle coke, and the coal bitumen is used as a binder. Graphite Electrodes has good electrical properties and chemical resistance, which has high mechanical strength at high temperature and good seismic performance.
China uhp hp rp graphite electrode for steel industry The graphite electrode is mainly made of petroleum coke and needle coke, and the coal bitumen is used as a binder. It is made by calcination, compounding, kneading, forming, baking, graphitization and machining. According to its quality indicators, graphite electrodes can be divided into RP graphite electrodes, HP graphite electrodes and UHP graphite electrodes. Our factory produce: 1. RP graphite electrode 2. HP graphite electrode 3. UHP graphite electrode Needle coke material , Low ash , low consumption!
Carbon graphite electrode manufacturer, diameter:100-700mm, length:1500-2700mm,
HP Size and Tolerance Diameter (mm) Length (mm) Nominal diameter Actual diameter Nominal length Tolerance Short feet length mm inch max min mm mm max min 200 8 209 203 1600/1800/ 2000/2200/ 2400/2700 ±100 -100 -275 250 10 258 252 300 12 307 302 350 14 357 352 400 16 409 403 450 18 460 454 500 20 511 505 550 22 556 553 600 24 613 607 Physical and Chemical Index of HP Items unit Diameter: 250-600mm Standard Test data Electrode Nipple Electrode Nipple Electrical resistance μΩm 6.5-7.5 6.0 6.0-7.0 5.5 Flexure strength Mpa 9.8-10.5 14 12-15 15-18 Modulus of elasticity GPa 12 16 12 14 Ash content % 0.2 0.2 0.2 0.2 Apparent density g/cm3 1.6 1.7 1.68-1.73 1.75 Factor of expansion(100-600) x10-6/ 2.4 2.2 2.2 2.0 Operating instruction 1. Use special hoist tools to hoist graphite electrode. It is strictly forbad to prize electrode ends up with crowbar. It must be handled with great care during transport to avoid being struck. 2. Graphite electrode must be kept away from being moistened or wetted by rain, snow and water, and must be kept dry. 3. Carefully checking before making connection, make sure that socket and nipple thread is not damaged, nipple pitch plug is in. 4. Blow the nipple and socket threads with compressed air. 5. It must be dried in the furnace before use, the drying temperature in the furnace should be less than 150,the drying period should be more 30 hours 6. Graphite electrode must be connected and contacted closely and straightly.Use moment spanner for connecting electrode with suitable force. Mustnt decline. 7. The holding device must hold the electrode tightly, good contact and no arc. 8. To avoid the electrode breakage, put the large materials in lower part and small materials in the upper part. Insulating materials should not be put into the furnace. The working current of electrode must be conformity with the allowable current of electrode in the instructions.
450mm Hp Uhp Graphite Electrodes Electrodes Graphite Uhp 400 Uhp 500 Graphite Electrodes Uhp 600 Graphite Electrodes Manufacturer supplier of RP HP UHP Grade Graphite Electrodes. RP HP UHP 200 250 300 350 400 450 500 600 650 700 Export to Kazakhstan, Uzbekistan, Iran, Egypt, South Africa, Italy, Oman, UAE, Russia. Ask us for Graphite Electrode prices
Mill scale, is formed on the outer surfaces of plates, sheets or profiles when they are being produced by rolling hot iron or steel billets in rolling or steel mills. It looks like a hard brittle sand and is mainly composed of iron oxides, mostly ferric, and is bluish black in color. Being produced during the reheating, conditioning and hot rolling operation for the production of steel articles, the mill scale initially adheres to the steel surface and protects it from atmospheric corrosion, provided no break occurs in this coating. From the chemical and physical analysis performed on the scrap, and according to the european environmental rules, the material has been classified as a special non dangerous waste, listed in green list In particular the mill scale can be classified as follows: Einecs (european commission no.): 266-007-8 Waste code: 10 02 10 Basel code: b 12 30 Hs code: 2619.00
This Cast Iron slag is a by-product derived from the production of thermal insulating products. The byproduct is a ferrous slag which can be utilised in an electric arc furnace to produce crude steel. Physical Description On visual inspection, it appears to be made up of irregular shapes. Dimension: 500mm -800mm Chemical Composition Its chemical composition is homogeneous and stable with Fe contents in the range of 90 +/- 5% and P contents < 0.6% S around 0.15% and C% around 3.5%. Packing: Loose in container Loading: in 20 Container For further information, please feel free to contact us.