Hengshui JingTong Rubber Co., Ltd.

What is PMMA plastic PMMA resin is also known as acrylic resin, organic glass or glass acrylic. Although not glass, in terms of technical surface, PMMA is quite similar to glass. PMMA is often used in the form of sheets and pieces with good impact resistance, high scratch resistance, and good light exposure. As a good economic alternative to glass, glass, Polycarbonate due to its low cost, it is suitable for projects that require good bearing capacity, difficult to break without high hardness MATERIAL:PMMA plastic repro pellet transparent yellowish CATEGORY: PMMA TYPE: repro pellet GRADE: Transparent Yellowish SPECIFICATION: Repro from film. Color tone is due to UVA additives Origin: Japan LOADING WEIGHT: 24 Ton FOB (USD/Ton): 1450$ - 1700$ Packaging: Jumbo Bag Est. Shipping Time: 15, 30, 45 days

POM Regrind from zipper Teeth, industry lump, industry runner Definition of POM resin (polyformaldehyde resin): polyformaldehyde is a linear polymer without side chain, high density and high crystalline properties. According to different chemical structures in the molecular chain, there are two types of homoformaldehyde and copolymers. of both types of polyformaldehyde density, high crystallinity, melting point, but thermal stability, the treatment temperature range is narrow (about 10oC), slightly lower in acid and alkali stability; The density of formaldehyde, melting point, strength and copolymer is lower, but good thermal stability, not easy to decompose, wide range of treatment temperature (about 50oC), acid and alkali stability are good . Plastic has excellent all-round performance. Good physical, mechanical and chemical properties, especially with excellent friction resistance. It is commonly referred to as steel or strip, which is the general engineering plastic third. Suitable for reducing wear on parts, transmitters, chemicals, tools and other parts. One of the synthetic resins, also known as polyformaldehyde resin, POM resin and steel, etc. This is a kind of white or black plastic resin with high hardness, high steel and high wear resistance. Used for gears, bearings, auto parts, machine tools, tools, etc. MATERIAL: POM Regrind from zipper Teeth , industry lump, industry runner CATEGORY: POM TYPE: Regrind SPECIFICATION: from zipper Teeth , industry lump, industry runner,Qty per month 52 mt Origin: Bangladesh LOADING WEIGHT: 24 Ton FOB (USD/Ton): 650$ - 850$ Packaging: Jumbo Bag Est. Shipping Time: 15, 30, 45 days

ABS Regrind ,Yes No Fr, NO pc abs, no iron, no circuit etc ABS has excellent mechanical properties, excellent impact resistance and can be used at extremely low temperatures. ABS has excellent wear resistance, good dimensional stability and oil resistance, and can be used for bearings under medium loads and speeds. ABS's creep resistance is greater than PSF and PC, but smaller than PA and POM. The flexural and compressive strength of ABS are poor in plastics. The mechanical properties of ABS are greatly influenced by temperature. ABS is flammable material and belongs to HB class according to UL94 standard. ABS burns quickly when ignited, and emits a lot of toxic gases and black smoke, which is not conducive to practical application. With the advancement of science and technology and improving the quality of life, everyone's safety awareness is getting stronger. The domestic and foreign countries have put in place strict fire and flame retardant requirements for plastic materials used in automobiles, construction, home appliances, office supplies, etc., and made corresponding technology. Standards and specifications, so research on ABS flame retardants has a very important meaning. MATERIAL: ABS Regrind ,Yes No Fr, NO pc abs, no iron, no circuit etc CATEGORY: ABS TYPE: Regrind SPECIFICATION: Regrind Abs from post consumer materials ,Yes No Fr, NO pc abs, no iron, no circuit etc. Qty per month 1 container 26 mt Origin: Bangladesh LOADING WEIGHT: 26 Ton FOB (USD/Ton): 750$ - 950$ Packaging: Jumbo Bag Est. Shipping Time: 15, 30, 45 days

Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.

Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.