Calcined Bauxite: Calcined Bauxite is obtained by calcining (heating) superior grade Bauxite at high temperature (from 850 oC to 1600 oC). This removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57 % to 58 % in raw Bauxite, Calcined Bauxite has an alumina content of 82 % to 86 %. The heating is carried out in rotary kilns. Calcination is done at different temperatures ranging from 850 oC to 1600 oC depending upon the customer’s application. We export Calcined Bauxite for various applications such as refractory bricks, abrasives, steel polishing, etc. We provide consistency in quality and availability of Calcined Bauxite at extremely competitive prices. Applications of Calcined Bauxite: Refractory Grade Calcined Bauxite (CB - I and CB - II Grade) : To make refractory grade, Bauxite is thermally treated at 1600 oC to produce Calcined Bauxite where the Alumina content is mostly above 82%. Brown Fused Alumina, Proppants and Road Surfacing : To make the above grades, Bauxite is thermally treated at 1000 oC - 1200 oC to produce Calcined Bauxite where the Alumina content is anywhere between 80-88% depending on the requirement. Minimum Order Quantity : 1 Containers
Features Of Calcined Bauxite Calcination is a process of heating, hence calcined bauxite is obtained by heating the high grade ore of the bauxite. Heating further removes the moisture content from the ore and thus results in the increase of the alumina content. Applications Abrasives Refractories Road surfacing
Calcined bauxite is produced by sintering/calcining with natural bauxite ore of low iron, low alkali at temperatures of 1600 - 1800 degree Celsius in the rotary kiln or round kiln through pre-heationg, calcination, cooling and other processes. During Calcining, it can be removed impurities and improving the content of alumina. Refractory grade bauxite has high refractoriness, good mechanical strength and moderate slag resistance. Therefore calcined bauxite is one of the most important raw materials for the production of shaped and unshaped refractories for the steel industry, foundries, glass and cement plants.
1) 47-48 GRADE CHEMICAL COMPOSITION (ON DRY BASIS) Al2O3 47-48%, Rejection Below 47% Silica 8-10%, Rejection Above 10% Fe2O3 8-12% Moisture 6-8%, 8% max (normal season), during rainy season 9% Max LOI 23% to 28% PHYSICAL COMPOSITION (ON NATURAL BASIS) Size: 0 mm to 100 mm (+/- 10%) CaO 1.5-2% - Rejection Above 2% TiO2 2.5%
We are exporter of Bauxite. Bauxite is a soft, whitish to reddish-brown rock consisting mainly of alumina-bearing hydroxides, oxides of iron, silicon and titanium with impurities of Ca, Mg, Cr, V, P, Ga and other elements. Raw Bauxite is a major source of aluminium. Basic alumina containing minerals of Bauxites are gibbsite Al(OH)3, Boehmite g-AlO(OH) and Diaspore a-AlO(OH) Bauxite is used in a lot of industries like the chemical industry, refractory, abrasive, cement, steel, and petrol industry amongst others. In chemical, bauxite along with alumina is used in the manufacturing of aluminium chemicals. In refractory, it is used as a raw material for making several products.
We can provide up to 10000 MT per month. SGS report is also available. The composition of bauxite consists mainly of aluminium hydroxide minerals, such as gibbsite Al(OH)3 along with various impurities such as iron oxides, silica, and titanium. The colour of bauxite can range from grey to brown, yellowish-brown, or reddish-brown, depending on the presence of impurities. Bauxite is a crucial raw material for the production of aluminium, which is widely used in various industries such as transportation, construction, packaging, electrical appliances, and aerospace. Aluminium is valued for its lightweight, corrosion resistance, high conductivity, and recyclability. Bauxite mining and aluminium production have significant economic impacts in countries with abundant reserves.