Antimony : The Antimony Is Silver-gray, High Friability At Ambient Temperature. Obtaining : - From Volatile Dusts And Anodic Sludge From Lead And Zinc Metallurgy. Use : - As An Alloying Element In Obtaining Tin-based Antifriction Alloys. - Obtaining The Lead-antimony Alloys Used In The Manufacture Of Automotive Batteries. Properties : - Silver-gray Color, High Friability At Ambient Temperature. Material Specification: According To Stas 10262/1975. Super Grade : Sb 99.95% Min; Pb 0.01% Max; As 0.01% Max. Presentation Form : Max. 15 Kg. Provenience : Import
Ferro Chromium : Iron Chromium Alloy With Chromium Content Ranging From 45 To 95%. Obtaining : - By Electrothermia, Reducing The Chromium Oxides By A Complex Scheme In Succession. Use : - Production Of Special And Anti-corrosive Alloy Steels; - In The Chemical Industry, Machine Building, Etc; - Manufacture Of Cutting Tools, Resistant To High Cutting Speeds. Ferro Carbon With High Fecr60c70 Chemical Composition : Cr 60% Min; C = 6.0 ÷ 8.0%; Si = 1.5% Max; P = 0.030% Max; S = 0.05% Max. Granulation : 5 ÷ 50mm; 10 ÷ 50mm; 10 ÷ 80mm; (90% Min). Packaging : Big Bags 1.000 Kg Ferro Carbon With Very Low Fecr 60 C 10 Chemical Composition : Cr 60% Min; C = 0.10% Max; Si = 1.5% Max; P = 0.050% Max; S = 0.030% Max. Granulation : 5 ÷ 50mm; 10 ÷ 50mm; 10 ÷ 80mm; (90% Min). Packaging : Big Bags 1.000 Kg
Ferroniobium : Niobium Iron Alloy, Having A Nickel Content Of 60 To 75% Obtaining : - Through Metalothermic Reduction Reactions (silicothermia Or Aluminotermia). Use : - Production Of Special Alloy And Anti-corrosive Alloys. Fenb 65 Material Specification : According To Sr Iso 5453/1996 Chemical Composition : Nb 60 ÷ 70%; Ta = 0.5% Max; Al = 1.0% Max; Si = 2.5% Max; Ti = 0.4% Max; C = 0.15% Max; P = 0.10% Max; S = 0.05% Max; Sn = 0.10% Max; Co = 0.05% Max. Granulation : 5 ÷ 50mm; 10 ÷ 50mm; (90% Min).
Ferro Silicon : Silicon Iron Alloy, Having A Silicon Content Of Between 40 And 90%; Typically Contains A Large Amount Of Iron Silicas And 1-2% Calcium. Ferrosiliconand Aluminum. Obtaining : - By Reducing The Silicon Dioxide (sio2, Natural Mineral = Quartz) At High Temperatures In Electric Furnaces. Use : - In The Production Of Alloyed Steels, Silicon Content Ensuring Good Deoxidation, As Well As Preventing The Decarburization Of Molten Steel; - Added To Gray Cast Iron, Increases Fluidity In Molten State. Chemical Composition : Si 72 ÷ 80%; Al = 1.5-2.0% Max; P = 0.05% Max; S = 0.04% Max; C = 0.20% Max. Granulation : 10 ÷ 50mm; 10 ÷ 80mm; 10 ÷ 100mm; (90% Min). Packaging : Big Bags 1.000 Kg.
Ferro Molybdenum : Iron Molybdenum Alloy Containing Molybdenum Content Between 55 And 75%. Obtaining : - By Carbon Reduction, But More Often Used In Practice Is The Silicotermic Reduction Method. Use : - Increasing The Mechanical Properties Of Steels; - Production Of Special And Anti-corrosive Alloy Steels. Femo 60 Chemical Composition : Mo 55 ÷ 65%; Si = 1.0% Max; C = 0.10% Max; P = 0.05% Max; S = 0.10% Max; Cu = 0.50% Max. Granulation : 5 ÷ 50mm; 10 ÷ 50mm; (90% Min). Packaging : Metal Barrels Of 250 Kg Femo 70 Chemical Composition : Mo 65 ÷ 75%; Si = 1.5% Max; C = 0.10% Max; P = 0.05% Max; S = 0.10% Max; Cu = 0.50% Max. Granulation : 5 ÷ 50mm; 10 ÷ 50mm; (90% Min). Packaging : Metal Barrels Of 250 Kg
Specifications: Total Moisture 6 % max, Ash (db) 6 % max, Volatile matter (db) 3 % max, Total Sulphur (db) 1 % max, Gross Calorific Value (db) 7700 kcal/kg, Net Calorific Value (db) 7600 kcal/kg, Fixed Carbon 88 % min, Phosphorus 0.02 % max. Size: 25-100 mm
Specifications: Total Moisture 10 % max, Ash (db) 11 % max, Volatile matter (db) 3 % max, Total Sulphur (db) 1 % max, Calorific Value (db) 7300 kcal/kg, Net Calorific Value (db) 7000 kcal/kg, Fixed Carbon 88 % min. Size: 6-13 mm
Specifications: Moisture 2 % max, Ash 6 % max, Volatile matter 3.5 % max, Total Sulphur 1 % max, Calorific Value 6500 kcal/kg, Fixed Carbon 90 % min. Packing: in big bags, with PE inlay of 10 kg, 500 kg or 1000 kg as per customer request Size: 0-3 mm, 1-3 mm, 3-8 mm
Foundry Cast Iron : L1-L6 according to GOST 4832-95; SR EN 10001 L1-L6 according to GOST 4832-95; SR EN 10001 Ingot : 12-18 kg