We are specialized in silica refractories for hot repairs of coke oven,glass furnace,which includes fused silica bricks,fused silica precast blocks,fused silica mortar,ceramic welding materials,conventional high duty silica bricks,silica mortar,fused silica ramming mix,gunning mix. Founder of our company is an expert of silica refracories in Sinosteel Refractories for more than 20 years.All the technical staff and control quality control staff are very expereienced,coming from Sinosteel Refractories,too.Passed qualification certification of ISO9001-2008. When the damage to the coke oven is so severe that holes could be observed,brick shaped fused silica precasted blocks have to be adopted to fill the gaps.The fused silica won't display observed thermal expansion,so no heat-up problems. Property of Fused Silica Precast Blocks Zero Expansion,so no heat-up problems Less joints,minimise the leakage of flue gas Save time and Equipment Application:for Hot Repair of Coke Oven,Revamp of Old Coke Battery,Ceramic Welding For further questions,please contact me: Contact: Judy Liu (Marketing&Sales)
Fused silica brick has better thermal shock resistance, much lower thermal expansion, and can be used to do hot repair. Fused Silica Brick for Hot Repair of Coke Oven is similar to general silica brick, but it has better thermal shock resistance. The property of fused silica brick is similar to general silica brick, but it has better thermal shock resistance, much lower thermal expansion and it can stand suddenly change of temperature. It also can be heated in very short time after buildup and do not need to calculate thermal expansion. So we can directly use its cold size for masonry. Put on wooden pallets, tightened with iron stripes, covered with plastic bag, warped with film, shipped in pallet by container. Do corner protection and other measures to avoid products from breaking. And these packages should be under ISPM standard.
Silica Brick for Coke Oven KNKSKS JG-94 Physical and chemical properties, dimension and appearance, strictly conform to DIN norm Application Construction of Coke Battery Coke Plant, Newly Built or Hot Repair
Magnesia Bricks Description Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750.. They are ideal products for glass furnace application. Magnesia Bricks Features: It is a kind of alkaline refractory product with periclase as main phase magnesite-alumina spinel clinker as basic material. the product has such characteristics as good temperature vibration, good strength and volume stability in high temperature. Magnesia Bricks Application Basic open-hearth furnace for steelmaking Electric furnace bottom and wall Permanent lining of oxygen converter Non-ferrous metal metallurgy furnace Hyperthermia tunnel kiln Lining of rotary cement kiln Heating furnace bottom and wall Regenerative chamber of glass furnace Magnesia Bricks Properties High Refractoriness Good alkaline slag erosion resistance High apparent initial softening temperature Good thermal conductivity High thermal expansion Magnesia Bricks Manufacturing Process Burnt Magnesia Bricks are manufactured with magnesite clinker as the raw material and fired in the high temperature of 1550~1600 after smashing, burdening, mulling and molding. High-purity products can be fired in the temperature that over 1750. Chemical bonded magnesite brick is produced with certain chemical bonding through mixing, molding and drying.
PRODUCT DATA SHEET ACID RESISTANT BRICK Material : RED SHALE Type Acid Resistant Brick Size (mm) 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions Heavy thermal shock Typical Physical Properties of GANESHAS Acid and Chemical Resistant Brick Characteristic RED SHALE ACID RESISTANT BRICK Test Standard Bulk Density, gm/cc - 2.3 to 2.35 ASTM C-20 -Water Absorption, % - 0.1 to 1.5 IS 4860-1968 Apparent Porosity, % -0.5 to 1.75 S 4860 Acid Solubility (H2SO4), Loss in Mass,% -0.1 to 1.8 ASTM C-279 Modulus of Rupture, PSI -2133 to 3555 ASTM C-67 Compressive Strength, Kg/cm2 - 700-900 IS 4860-1968 Abrasion Resistant , Volume in mm3 -69 to 85 EN 102 Surface Hardness, MOHS Scale - 7
PRODUCT DATA SHEET ACID RESISTANT BRICK Material : FIRECLAY Type Acid Resistant Brick Size (mm) : 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : * We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: * Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions - Heavy thermal shock Characteristic Fireclay Type Acid Resistant Brick - Test Standard Bulk Density, lbs/ft3 - 2.25 to 2.30 ASTM C-20 Water Absorption, % - 0.1 to 1.8 ASTM C-20 Apparent Porosity, % - 4.05 to 4.14 ASTM C-20 Acid Solubility (H2SO4), Loss in Mass,% - 6.1 to 6.8 ASTM C-279 Modulus of Rupture, Mpa - 14.6 ASTM C-67 Compressive Strength, PSI - 15500 to 17250 ASTM C-67 Abrasion Resistant , Volume in mm3 - 71 to 96 EN 102 Surface Hardness, MOHS Scale - 7 Thermal Conductivity, BTU-in/hr-ft-F - 6.94 to 7.12 ASTM C-236 Thermal Expansion Coefficient,in/in/Fx10-6 - 2.6 to 2.8 EN 103
Supplier: Refractory bricks, high alumina bricks, acid proof bricks, tiles and castables, all mortars and fire clay, low cement castables, insulating castables, conventional dense refractory bricks, insulation bricks, cold face, hot face insulation bricks, hot face insulation bricks, acid resistant bricks/components, membranes, acid resistant cement, construction chemicals, class 1 ar tiles and bricks 38mm and 75mm, 4457 vitrified ar tiles with 0% water absorption, 20mm & 25m, primer, mastics, pot. silicate cement, coerce cement, furnace based cement, crushed refractory boiler bed material, acid resistant tiles, acid resistant brick fireclay type, acid resistant brick red shale type, bitumen primer, epoxy resin & hardner, furan powder and syrup solution,
Technical Data Sheet Of Accoset-50 ALUMINA MORTAR (Test Certificate) General Properties A. Max service temperature - 1500 oC B. Maximum grain size - 0 - 1.5 mm C. Water required for mixing - 22 - 30% D. Setting - Airsetting E. Sintering Temp - 1550 oC Chemical Properties A. Al2O3 - 50.00% B. SiO2 - 31.00% c. Fe2O3 - 5.00% D. LOI - 7.00% Physical Properties A. Dry Density - kg / m3 B. CCS - 17 kg / cm2 after drying at 110C / 24 hr C. MOR - 20 kg / cm2 at 110 oC/ 24 hr 18 kg/cm2 at 800 C/ 3 hr Thermal Properties - A. Refractoriness ( Orton / C) - 31.5 orton cone/1699 oC Packaging - 25 - 50 kg bags Storage Life - 12 months Delivery State - Dry
Insulation Bricks