*More than 10 years manufacturer and supplier experience *Quick delivery of 15 days. *Australian Standard: AS/NZS 2208: 1996-safety glazing matererials *Safety strong packing and loading *Option processing clear, frosted, heat soaked, heat strengthened *Edging: Flat edge, grind edge, polished edge, beveled edge and others. Tempered Glass/Toughened Glass Tempered glass is made by heating float glass to its softening point ( 650-700 C )and then suddenly cooling down to form compression in the surface layer of the glass, thus the mechanical strength is increased by 5 times. Features: 1.5 times harder than ordinary float glass. 2. Tensile strength for float glass 40 MPa (N/mm2), tempered glass, 120-200 MPa (N/mm2) 3. Quality standard AS/NZS 2208: 1996 4. It withstands abrupt temperature change of 220 Centigrade. 5. Once breakage occurs, the glass disintegrates into small cubical fragments, which are relatively harmless to human body. Heat Strengthened Tempered Glass 1. Better flatness than tempered glass 2. Effectively resist the effect of thermal stress, avoid glass thermal explosion 3. Withstand a very wide range of rapid temperature changing with endurance of 200-300 C 4. Cooling rate lower and surface stress smaller than tempered glass Use high quality raw clear glass, visible light transmittance(%) from 4mm-19mm Specification: Flat Tempered Glass MIN 90x90mm, Max 3660x2140mm Thickenss 4mm, 5mm, 6mm, 8mm, 10mm, 12mm, 15mm, 19mm Bent/Curved Tempered Glass Max. Size 2200x750(mm) Min Size 400*300(mm) Thickness 5-19(mm) Min. Benting Radius 370mm Applications: 1. External use of windows, doors, curtain wall, shopfronts, offices, houses, shops etc. 2. Interior glass screens, partitions, balustrades etc. 3. Shop display windows, showcases, display shelves etc. 4. Furniture, table-tops, picture frames etc. Tempered Glass Equipments 1. Water jet machine, cutting tolerance +-0.1mm 2. Screen Printing Equipment 3. Single Straight-line Glass Edging Machine 4. Double Straight-line Glass Edging Machine 5. Round Glass Edging Machine 6. Glass Drilling Machine 7. Glass Tempering Furnace 8. Glass cutting line Packing detail: 1. Interlay paper between two sheets 2. Timber end caps 3. Iron/plastic belt for consolidation 4. Safety corner Density 2.5g/cm Tensile Strength 120-200 MPa (N/mm2) Compressive Strength 1000 N/mm 2 Yong's Module 73 Gpa Coefficient of linear expansion 9 x 10 - 6 m/Mk softening point 650-700C Thickness4mm,5mm,6mm,8mm,10mm,12mm,15mm,19mm Payment term (1) 30% deposit ,balance paid against the copy of B/L payment term (2) 30% deposit ,balance will be L/C at sight Delivery time 15 days after received the deposit Packing End caps pakcing within stripe and paper MOQ 1000 Square meter Loading port Qingdao port Australian Standard: AS/NZS 2208:1996-safety glazing matererials